Effects of repeated loading on the fracture behavior of notched TiAl specimens | |
Cao, R.1; Chen, J. H.1; Zhang, J.2; Zhu, H.1 | |
2008-09 | |
发表期刊 | ENGINEERING FRACTURE MECHANICS |
ISSN | 0013-7944 |
卷号 | 75期号:14页码:4019-4035 |
摘要 | Notched specimens of a fully lamellar TiAl alloy and a duplex TiAl alloy were in situ tensile tested with repeated loading-unloading-reloading processes in a scanning electron microscope (SEM). The step-by-step processes of initiation and extension of the main crack were captured by SEM. The fracture surfaces were observed and one-sector-to-one-sector related to the crack extension. Effects of loading-unloading damage on the fracture behavior were evaluated by combining the pictures of propagating crack configurations, corresponding fracture surfaces and the load locus. The results revealed the following events: (1) at the elastic regime, the loading-unloading process had negligible effect on the fracture behavior produced by subsequent reloading; (2) at the plastic regime, even at a value much lower than that of the preload, the reload extended further the existing main crack; (3) after a heavy loading-unloading process, the main crack extended and resulted in final fracture at a value of the reload, which was lower than that of the preload and (4) microcracks produced in the loading-unloading process had minor effects on the fracture behavior. (c) 2008 Elsevier Ltd. All rights reserved. |
关键词 | TiAl alloy in situ tensile test notched specimen microcracks |
DOI | 10.1016/j.engfracmech.2008.03.015 |
收录类别 | SCI ; SCIE |
语种 | 英语 |
WOS研究方向 | Mechanics |
WOS类目 | Mechanics |
WOS记录号 | WOS:000257350300001 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
EI入藏号 | 20082311299530 |
EI主题词 | Titanium alloys |
EI分类号 | 542.3 Titanium and Alloys - 931.1 Mechanics - 951 Materials Science |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/35475 |
专题 | 材料科学与工程学院 |
通讯作者 | Chen, J. H. |
作者单位 | 1.Lanzhou Univ Technol, Off President, State Key Lab Adv Nonferrous Met Mat, Lanzhou 730050, Gansu, Peoples R China 2.Cent Iron & Steel Res Inst, High Temp Mat Res Div, Beijing 100081, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Cao, R.,Chen, J. H.,Zhang, J.,et al. Effects of repeated loading on the fracture behavior of notched TiAl specimens[J]. ENGINEERING FRACTURE MECHANICS,2008,75(14):4019-4035. |
APA | Cao, R.,Chen, J. H.,Zhang, J.,&Zhu, H..(2008).Effects of repeated loading on the fracture behavior of notched TiAl specimens.ENGINEERING FRACTURE MECHANICS,75(14),4019-4035. |
MLA | Cao, R.,et al."Effects of repeated loading on the fracture behavior of notched TiAl specimens".ENGINEERING FRACTURE MECHANICS 75.14(2008):4019-4035. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Cao-2008-Effects of (5315KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[Cao, R.]的文章 |
[Chen, J. H.]的文章 |
[Zhang, J.]的文章 |
百度学术 |
百度学术中相似的文章 |
[Cao, R.]的文章 |
[Chen, J. H.]的文章 |
[Zhang, J.]的文章 |
必应学术 |
必应学术中相似的文章 |
[Cao, R.]的文章 |
[Chen, J. H.]的文章 |
[Zhang, J.]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论