Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy | |
Wang, Xi-Jing1,2![]() ![]() | |
2009-03-01 | |
发表期刊 | Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals
![]() |
ISSN | 10040609 |
卷号 | 19期号:3页码:484-489 |
摘要 | The microstructure and property before and after heat treatment of friction stir welded 5 mm aero 7075 aluminum alloy were investigated. The results show that when the rotating speed of stirring joint is 600 r/min and the welding speed is 60 mm/min, the tensile strength can reach 381 MPa that is 84.6% of the base metals, which are regarded as the most ideal parameters under experimental conditions. There are equiaxed grains with size of 6-7 μm in weld nugget. After heat treatment, the tensile strength can reach 415 MPa. The lowest hardness appears in thermomechanically affected zone (TMAZ) of advancing side. The fractography has a characteristic of dimples of strengthening phase and the strain fracture appears in TMAZ of advancing side of joints. The weak point of friction stir welding joint for 7075 aluminum alloy occurs in the TMAZ. |
关键词 | After-heat treatment Aluminum alloys Fracture mechanics Friction High strength alloys Microstructure Research laboratories Tensile strength Textures 7075 aluminum alloy Effects of heat treatment Experimental conditions Friction stir welding joints High strength aluminum alloys Microstructure and properties Strengthening phase Thermomechanically affected zones |
收录类别 | EI |
语种 | 中文 |
出版者 | Central South University of Technology |
EI入藏号 | 20091712054487 |
EI主题词 | Friction stir welding |
EI分类号 | 531.1 Metallurgy - 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 901.3 Engineering Research - 931.1 Mechanics - 951 Materials Science |
来源库 | Compendex |
分类代码 | 531.1 Metallurgy - 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 901.3 Engineering Research - 931.1 Mechanics - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/111599 |
专题 | 材料科学与工程学院 机电工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Non-Ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 兰州理工大学; 材料科学与工程学院 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Wang, Xi-Jing,Sun, Gui-Ping,Zhang, Jie,et al. Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy[J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,2009,19(3):484-489. |
APA | Wang, Xi-Jing,Sun, Gui-Ping,Zhang, Jie,Xu, Cheng,Li, Shu-Wei,&Niu, Yong.(2009).Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy.Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,19(3),484-489. |
MLA | Wang, Xi-Jing,et al."Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy".Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals 19.3(2009):484-489. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论