题名 | 溶胶-凝胶法制备纳米ATO粉体和薄膜及其结构与性能的研究 |
作者 | 钟小华 |
学位类型 | 硕士 |
导师 | 杨保平 ; 贾均红 |
答辩日期 | 2008 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 化学工艺 |
关键词 | sol-gel法 纳米ATO粉体和薄膜 方块电阻 光透过率 荧光性能 |
摘要 | 二氧化锡(SnO2)是一种具有直接带隙的宽禁带N型半导体材料,300K时其禁带宽度为3.62eV,室温下电阻率较高,当产生氧空位或掺杂元素后形成N型半导体,具有导电性能。锑掺杂二氧化锡(Antimony doped Tin Oxide, ATO)作为透明导电薄膜由于具有优良的导电性能、光学性能、稳定性好和灵敏度高等优点,广泛应于太阳能电池、电致变色材料、防辐射抗静电材料、气敏元件、电极材料等方面。 |
其他摘要 | Tin oxide (SnO2) is an n-type wide energy gap semiconductor oxide, the energy gap is 3.62 eV at 300 K, and its resistivity is very high at room temperature. Oxygen vacancies and extrinsic dopants can increase the concentration of charge carrier in SnO2 and thus the conductivity is further increased. Antimony-doped tin oxide (ATO) is an important member of the transparent conductive oxides and widely used in solar cells, electrochromic materials, anti-radiation and anti-static materials, gas sensors, transparent electrodes for its high electrical conductivity, high optical transmission, good stability and high sensibility. |
页数 | 59 |
语种 | 中文 |
学号 | 082081702014 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/98771 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 钟小华. 溶胶-凝胶法制备纳米ATO粉体和薄膜及其结构与性能的研究[D]. 兰州理工大学,2008. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[钟小华]的文章 |
百度学术 |
百度学术中相似的文章 |
[钟小华]的文章 |
必应学术 |
必应学术中相似的文章 |
[钟小华]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论