| 题名 | 铸钢表面渗层摩擦性能的研究 |
| 作者 | 张巨银 |
| 学位类型 | 硕士 |
| 导师 | 郝远 ; 杨贵荣 |
| 答辩日期 | 2007 |
| 学位授予单位 | 兰州理工大学 |
| 学位名称 | 工学硕士 |
| 学位专业 | 黑色金属表面改性 |
| 关键词 | 负压铸渗 滑动摩擦 高温摩擦 |
| 摘要 | 导卫板是钢材轧制生产线上重要的辅助装置，它主要用于诱导、夹持轧件（钢丝）顺利通过，在实际生产中，导卫板的磨损破坏非常严重，因此导卫板材料的创新以及改良显得十分必要，本论文以导卫板应用为背景，采用负压铸渗工艺在ZG45表面制备了一层耐磨、耐高温氧化的镍基渗层和ZrO2/Ni复合渗层。 |
| 其他摘要 | Guide plate is an important accessory device for steel line rolling production which mainly used for induction,gripping roller piece (steel) passed.In the action production the plate wear damage is very serious.Based on the guide plate special working condition.Guide plate material has become really important for innovation and improvement.In this paper a wear-resistant and high temperature oxidation-resistant of the infiltrated Ni based layer and composite layer of ZrO2/Ni were produced on the ZG45 surface through vacuum infiltration technique according to the work condition of guide plate. |
| 页数 | 58 |
| 语种 | 中文 |
| 学号 | 072080502019 |
| 文献类型 | 学位论文 |
| 条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/98049 |
| 专题 | 兰州理工大学 |
| 作者单位 | 兰州理工大学 |
| 第一作者单位 | 兰州理工大学 |
| 推荐引用方式 GB/T 7714 | 张巨银. 铸钢表面渗层摩擦性能的研究[D]. 兰州理工大学,2007. |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 查看访问统计 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [张巨银]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [张巨银]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [张巨银]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论