题名 | Ni-Cr-Mo-Cu合金的耐蚀性能研究 |
作者 | 吕学飞 |
学位类型 | 硕士 |
导师 | 杨瑞成 |
答辩日期 | 2003 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料学 |
关键词 | 通用性镍基耐蚀合金 APF 浸蚀 电化学腐蚀 阳极极化 高温氧化 氧化动力学 |
摘要 | 作为机械零部件三种主要失效形式之一,腐蚀问题直接关系到国民经济各个领域。鉴于此,本文依据质量百分因子(APF=4Cr/(2Mo+W))法,并参考现今先进耐蚀合金,通过向镍中添加铬、钼和铜元素,设计了7种通用性Ni-Cr-Mo-Cu耐蚀合金。采用手工电弧炉熔炼,制备出Ni-Cr-Mo-Cu耐蚀合金,并在1140℃保温2.5h固溶处理。针对所制试样,从浸蚀、电化学腐蚀和高温氧化三个方面进行耐蚀性能及其机理的研究。 |
其他摘要 | As one of three kinds of failure modes of the mechanical components, corrosion of metals connects with all regions of economy directly. Therefore, based on the APF factor method and referencing to nowadays advance corrosion resistant alloys, seven schemes versatile Ni-Cr-Mo-Cu corrosion resistant alloys were designed and prepared by manual electro- arc furnaces in this thesis. Alloys were solution-treated at 1140℃ for 2.5h. Corrosion resistance and mechanisms of these alloys were researched through erosion, electrochemical corrosion and high temperature oxidation. |
页数 | 58 |
语种 | 中文 |
学号 | P0308050225 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/95746 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 吕学飞. Ni-Cr-Mo-Cu合金的耐蚀性能研究[D]. 兰州理工大学,2003. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[吕学飞]的文章 |
百度学术 |
百度学术中相似的文章 |
[吕学飞]的文章 |
必应学术 |
必应学术中相似的文章 |
[吕学飞]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论