Effect of Copper Tailing Content on Corrosion Resistance of Steel Reinforcement in a Salt Lake Environment | |
Zhang, Liming1; Li, Jia2; Qiao, Hongxia3![]() | |
2019-10 | |
发表期刊 | MATERIALS
![]() |
卷号 | 12期号:19 |
摘要 | With the increasing proportions of copper tailings of concrete in the Qinghai Salt Lake area of China, there arises the problem of corrosion of steel reinforcement in concrete structures. In this study, we determine the corrosion rate (C-R), crack width, and corrosion potential of the steel reinforcement with copper tailing. This was achieved by conducting the constant-current accelerated corrosion test with different proportions of copper tailing in the brine environment of the Qinghai province. The results demonstrate that the corrosion potential (E-corr) and the passivation area of the polarization curve decrease with the increase in the corrosion time, and the corrosion rate and crack width increase with the increase in the corrosion time. When the corrosion time is the same, the corrosion potential, crack width, and corrosion depth of the reinforcement decrease first and then increase with the increase in the copper tailing powder content. When the copper tailing powder content is 20%, the above parameters reach the minimum value. In the salt lake environment of Qinghai, China, the copper tailing powder content is recommended to be 20%. |
关键词 | copper tailing Qinghai Salt Lake constant-current acceleration corrosion resistance |
DOI | 10.3390/ma12193069 |
收录类别 | SCI |
语种 | 英语 |
资助项目 | Science and Technology Project of the Jiangxi education department[GJJ180930] ; National Key Research and Development Plan "Solid Waste Resources" Key Projects[2018YFC1903402] |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Multidisciplinary |
WOS记录号 | WOS:000493308500018 |
出版者 | MDPI |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/76576 |
专题 | 土木工程学院 |
通讯作者 | Zhang, Liming |
作者单位 | 1.Nanchang Inst Technol, Sch Civil & Architectural Engn, Nanchang 330099, Jiangxi, Peoples R China 2.Nanchang Inst Technol, Library, Nanchang 330099, Jiangxi, Peoples R China 3.Lanzhou Univ Technol, Sch Civil Engn, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Liming,Li, Jia,Qiao, Hongxia. Effect of Copper Tailing Content on Corrosion Resistance of Steel Reinforcement in a Salt Lake Environment[J]. MATERIALS,2019,12(19). |
APA | Zhang, Liming,Li, Jia,&Qiao, Hongxia.(2019).Effect of Copper Tailing Content on Corrosion Resistance of Steel Reinforcement in a Salt Lake Environment.MATERIALS,12(19). |
MLA | Zhang, Liming,et al."Effect of Copper Tailing Content on Corrosion Resistance of Steel Reinforcement in a Salt Lake Environment".MATERIALS 12.19(2019). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论