Effect of La addition on semi-solid microstructure evolution of Mg-7Zn magnesium alloy | |
Zhang, Zhan-yu; Huang, Xiao-feng; Yang, Fan; Zhang, Sheng; Fu, Jiao-li | |
2022-09 | |
发表期刊 | CHINA FOUNDRY |
ISSN | 1672-6421 |
卷号 | 19期号:5页码:403-410 |
摘要 | Semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys were prepared by semi-solid isothermal heat treatment. The effects of the La element on the as-cast and semi-solid microstructures of Mg-7Zn alloy were investigated. Meanwhile, the effects of isothermal temperature and holding time on the evolution of the semi-solid microstructure of Mg-7Zn-0.3La alloy were also studied. Results indicate that the addition of a small amount of La can significantly refine the as-cast and semi-solid microstructure. During the semi-solid thermal transformation, the size and shape factor of solid particles decrease at first and then increase with the increase of isothermal temperature and holding time. The semi-solid microstructure of Mg-7Zn-0.3La alloy obtained by holding at 605 degrees C for 30 min is the optimal. The average size of solid particles, shape factor, and solid fraction are 42 urn, 1.45 and 61.8%, respectively. At the same time, a comparative study on the coarsening process of particles in the semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys reveals that the addition of La effectively decreases the coarsening rate of solid particles and restricts the growth of solid particles. |
关键词 | magnesium alloy La element semi-solid microstructure evolution coarsening rate constant TG146 22 A |
DOI | 10.1007/s41230-022-1191-2 |
收录类别 | SCIE ; EI |
语种 | 英语 |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
WOS类目 | Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000823246400001 |
出版者 | SPRINGER SINGAPORE PTE LTD |
EI入藏号 | 20233414604016 |
来源库 | WOS |
原始文献类型 | Journal article (JA) |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/159438 |
专题 | 材料科学与工程学院 理学院 |
通讯作者 | Huang, Xiao-feng |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Zhang, Zhan-yu,Huang, Xiao-feng,Yang, Fan,et al. Effect of La addition on semi-solid microstructure evolution of Mg-7Zn magnesium alloy[J]. CHINA FOUNDRY,2022,19(5):403-410. |
APA | Zhang, Zhan-yu,Huang, Xiao-feng,Yang, Fan,Zhang, Sheng,&Fu, Jiao-li.(2022).Effect of La addition on semi-solid microstructure evolution of Mg-7Zn magnesium alloy.CHINA FOUNDRY,19(5),403-410. |
MLA | Zhang, Zhan-yu,et al."Effect of La addition on semi-solid microstructure evolution of Mg-7Zn magnesium alloy".CHINA FOUNDRY 19.5(2022):403-410. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论