Effects of remelting temperature on the microstructure evolution of Ni60/WC directional structure coating | |
Yang, Xiaotian1,2![]() | |
2022-04-05 | |
发表期刊 | Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University
![]() |
ISSN | 1006-7043 |
卷号 | 43期号:4页码:587-592 |
摘要 | To improve the microstructure performance of the directional structure of the composite coating, the tungsten carbide-reinforced Ni60/WC directional structure coating is prepared by using flame spraying, induction remelting, and forced cooling technologies. The microstructure, phase, and microhardness of the coating are analyzed comparatively using a metallographic microscope, scanning electron microscope, X-ray diffractometer, and microhardness tester. The effects of induction remelting temperature on the microstructure evolution and properties of the directional structure of the composite coating are investigated, thus revealing the formation and strengthening mechanisms of the coating. Results show that, as the remelting temperature increases, the microstructure of the coating changes from fine and condensed microstructure at low remelting temperature to oriented microstructure growing along heat flow at high remelting temperature. When the temperature is 1 200 , the oriented structure of the coating becomes much more apparent. The additive dissolves at first, diffuses in grain boundary to form network eutectic, gradually transforms into a massive structure, and finally fills and strengthens the grain boundary again at 1 200 . The condensed structure of the coating at low temperatures increases the hardness of the coating's cross-section. The coating whose directional structure was formed at a high temperature of 1 200 had the highest level of hardness. Appropriate remelting temperature can effectively improve the properties of WC reinforced Ni60 directional structure coating. Copyright ©2022 Journal of Harbin Engineering University. |
关键词 | Composite coatings Flame spraying Grain boundaries Microstructure Nickel compounds Reinforcement Remelting Scanning electron microscopy Tungsten carbide Vickers hardness Composites coating Cooling technology Directional structure Forced cooling Grain-boundaries Induction remelting Microstructure evolutions Microstructure performance Temperature increase Tungsten carbide particles |
DOI | 10.11990/jheu.202104040 |
收录类别 | EI |
语种 | 中文 |
出版者 | Editorial Board of Journal of Harbin Engineering |
EI入藏号 | 20222112159478 |
EI主题词 | Microhardness |
EI分类号 | 534.1 Foundries ; 804.2 Inorganic Compounds ; 813.1 Coating Techniques ; 813.2 Coating Materials ; 817.2 Polymer Applications ; 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/158371 |
专题 | 学报编辑部 |
作者单位 | 1.School of Materials and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Wenzhou Pump and Valve Engineering Research Institute, Lanzhou University of Technology, Wenzhou; 325105, China; 3.Chongqing Key Laboratory of Environmental Materials and Remediation Technology, Chongqing University of Arts and Sciences, Chongqing; 402160, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Yang, Xiaotian,Wei, Hengli,Zhou, Jun,et al. Effects of remelting temperature on the microstructure evolution of Ni60/WC directional structure coating[J]. Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University,2022,43(4):587-592. |
APA | Yang, Xiaotian,Wei, Hengli,Zhou, Jun,Wang, Xinhua,Zeng, Rong,&Yang, Qiangbin.(2022).Effects of remelting temperature on the microstructure evolution of Ni60/WC directional structure coating.Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University,43(4),587-592. |
MLA | Yang, Xiaotian,et al."Effects of remelting temperature on the microstructure evolution of Ni60/WC directional structure coating".Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University 43.4(2022):587-592. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论