Research on Microstructure and Properties of Mg-1.5Zn-0.2Ca Alloy Extruded at Moderate Temperature | |
Zhang, Hongfei1,2; Ding, Yutian1,2; Lei, Jian1,2; Shen, Yue1,2; Chen, Jianjun1,2; Gao, Yubi1,2 | |
2022-02-10 | |
发表期刊 | Cailiao Daobao/Materials Reports |
ISSN | 1005-023X |
卷号 | 36期号:3 |
摘要 | Grain refinement can effectively improve the mechanical properties of magnesium alloy. Based on this, study was conducted on the Mg-1.5Zn-0.2Ca alloy and the microstructure of its alloys was regulated by moderate temperature extrusion process. The analysis of extruded alloy showed that, with decreasing of extrusion temperature, the deformation model of Mg-1.5Zn-0.2Ca alloy gradually changes, at the same time the grain size of extruded alloys also decreases, and the extruded alloys exhibit much better mechanical properties. The alloy is dominated by combination of basal slip and twining when extruded at 280 , gaining the dynamic recrystallized (DRXed) grains for average size of 5.3 μm, while the yield strength, ultimate tensile strength and elongation are 95 MPa, 186 MPa and 22%, respectively. © 2022, Materials Review Magazine. All right reserved. |
关键词 | Calcium alloys Dynamics Extrusion Grain refinement Grain size and shape Magnesium alloys Tensile strength Ternary alloys Zinc alloys Basal slip Deformation modeling Dynamic recrystallisation Extruded alloys Extrusion process Extrusion temperatures Grainsize Mg-1.5zn-0.2ca alloy Microstructure and properties Moderate temperature |
DOI | 10.11896/cldb.20120264 |
收录类别 | EI |
语种 | 中文 |
出版者 | Cailiao Daobaoshe/ Materials Review |
EI入藏号 | 20220911731983 |
EI主题词 | Dynamic recrystallization |
EI分类号 | 531.1 Metallurgy ; 542.2 Magnesium and Alloys ; 546.3 Zinc and Alloys ; 549.2 Alkaline Earth Metals |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/158050 |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Zhang, Hongfei,Ding, Yutian,Lei, Jian,et al. Research on Microstructure and Properties of Mg-1.5Zn-0.2Ca Alloy Extruded at Moderate Temperature[J]. Cailiao Daobao/Materials Reports,2022,36(3). |
APA | Zhang, Hongfei,Ding, Yutian,Lei, Jian,Shen, Yue,Chen, Jianjun,&Gao, Yubi.(2022).Research on Microstructure and Properties of Mg-1.5Zn-0.2Ca Alloy Extruded at Moderate Temperature.Cailiao Daobao/Materials Reports,36(3). |
MLA | Zhang, Hongfei,et al."Research on Microstructure and Properties of Mg-1.5Zn-0.2Ca Alloy Extruded at Moderate Temperature".Cailiao Daobao/Materials Reports 36.3(2022). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论