The tribological performance of W-DLC in solid-liquid lubrication system addivated with Cu nanoparticles

doi:10.1088/2051-672X/ac4086

IR > 理学院

	The tribological performance of W-DLC in solid-liquid lubrication system addivated with Cu nanoparticles
	Li, Dongshan 1; Kong, Ning 1; Li, Ruishan2 ; Zhang, Boyang 1; Zhang, Yongshun 3; Wu, Zhiguo 3; Zhang, Qingdong 1
	2021-12
发表期刊	SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES
ISSN	2051-672X
卷号	9 期号:4
摘要	Judicious selection of additives having chemical and physical compatibility with the DLC films may help improving the triboligical properties and durability life of DLC-oil composite lubrication systems. In this study, Cu nanoparticles were added to PAO6 base oil to compose a solid-liquid composite lubrication system with W-DLC film. The effects of nanoparticle concentration, test temperature and applied load on tribological performance were systematically studied by a ball-on-disk friction test system. The tribological results illustrated that Cu nanoparticles could lower the coefficient of friction (COF) and dramatically reduce the wear rates of W-DLC films. The optimal tribological behavior was achieved for the 0.1 wt% concentration under 30 degrees C and the applied load of 100 N. The test temperature and applied load were vital influencing factors of the solid-liquid lubrication system. The bearing effect and soft colloidal abrasive film of spherical Cu nanoparticle contributed to the excellent tribological performance of the composite lubrication system under mild test conditions, meanwhile, the local delamination of W-DLC film and oxidation were the main causes of the friction failure under harsh test conditions. With test temperature and applied loads increase the degree of graphitization of the W-DLC film increased. In conclusion, there are several pivotal factors affecting the tribological performance of solid-liquid lubrication systems, including the number of nanoparticles between rubbing contact area, graphitization of the worn W-DLC films, tribofilms on the worn ball specimens and oxidation formed in friction test, and the dominant factor is determined by the testing condition.
关键词	Cu nanoparticles W-DLC films solid-liquid composites lubrication
DOI	10.1088/2051-672X/ac4086
收录类别	SCIE
语种	英语
WOS研究方向	Engineering ; Instruments & Instrumentation ; Materials Science
WOS类目	Engineering, Mechanical ; Instruments & Instrumentation ; Materials Science, Multidisciplinary
WOS记录号	WOS:000730934700001
出版者	IOP Publishing Ltd
来源库	WOS
引用统计	被引频次：1[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	https://ir.lut.edu.cn/handle/2XXMBERH/154974
专题	理学院
通讯作者	Kong, Ning
作者单位	1.Univ Sci & Technol Beijing, Sch Mech Engn, Beijing 100083, Peoples R China; 2.Lanzhou Univ Technol, Sch Sci, Lanzhou 730050, Peoples R China; 3.Gansu Acad Sci, Inst Nanomat Applicat Technol, Lanzhou 730000, Peoples R China
推荐引用方式 GB/T 7714	Li, Dongshan,Kong, Ning,Li, Ruishan,et al. The tribological performance of W-DLC in solid-liquid lubrication system addivated with Cu nanoparticles[J]. SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES,2021,9(4).
APA	Li, Dongshan.,Kong, Ning.,Li, Ruishan.,Zhang, Boyang.,Zhang, Yongshun.,...&Zhang, Qingdong.(2021).The tribological performance of W-DLC in solid-liquid lubrication system addivated with Cu nanoparticles.SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES,9(4).
MLA	Li, Dongshan,et al."The tribological performance of W-DLC in solid-liquid lubrication system addivated with Cu nanoparticles".SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES 9.4(2021).