Life Prediction and Long-Term Durability of Coated Steel Bars in Magnesium Oxychloride Concrete | |
Wang, Penghui1; Qiao, Hongxia1,2; Chen, Kefan1; Li, Yuanke1; Feng, Qiong1 | |
2020-07 | |
发表期刊 | KSCE Journal of Civil Engineering |
ISSN | 12267988 |
卷号 | 24期号:7页码:2120-2131 |
摘要 | The solution to the problem of corrosion of the steel bars in magnesium oxychloride cement concrete (MOCC) is to apply a coating that protects the steel. To investigate the coating’s long- term protective effect on the steel, a solution immersion accelerated corrosion test was carried out on coated reinforced MOCC for up to 2,160 days. Electrochemical tests were conducted every 90 days to measure the polarization curve and AC impedance during the steel bars’ corrosion process. Then, the corrosion current density that characterizes the corrosion of a coated steel bar was used as a degradation index, and the time to the coated steel bar’s corrosion was predicted based on the Wiener function. It was concluded that after 2,160 days of solution immersion, the coated steel bars’ corrosion current density was 0.063 µA·cm−2, indicating that the coating protected the steel bars in MOCC from corrosion well. Thdroughout the immersion process, the specimen’s corrosion current density showed a steady and increasing trend, and its polarization impedance showed a volatile growth trend. The degradation of the coated steel bars also obeyed the Wiener degradation process, and the bars reached a severely rusted state at 21,800d with a corrosion time of R0.6(t) is 10,650d. © 2020, Korean Society of Civil Engineers. |
关键词 | Bars (metal) Concretes Current density Magnesium compounds Polarization Steel corrosion Steel testing Accelerated corrosion tests Corrosion current densities Electrochemical test Long term durability Magnesium oxychloride Magnesium oxychloride cement Polarization curves Polarization impedance |
DOI | 10.1007/s12205-020-1970-5 |
收录类别 | EI ; SCIE |
语种 | 英语 |
WOS研究方向 | Engineering |
WOS类目 | Engineering, Civil |
WOS记录号 | WOS:000534835500001 |
出版者 | Springer Verlag |
EI入藏号 | 20202108697032 |
EI主题词 | Corrosion resistant coatings |
EI分类号 | 412 Concrete ; 535.1.2 Rolling Mill Practice ; 545.3 Steel ; 701.1 Electricity: Basic Concepts and Phenomena |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/150999 |
专题 | 土木工程学院 |
通讯作者 | Qiao, Hongxia |
作者单位 | 1.Lanzhou Univ Technol, Key Lab Disaster Prevent & Mitigat Civil Engn Gan, Lanzhou 730050, Peoples R China; 2.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Wang, Penghui,Qiao, Hongxia,Chen, Kefan,et al. Life Prediction and Long-Term Durability of Coated Steel Bars in Magnesium Oxychloride Concrete[J]. KSCE Journal of Civil Engineering,2020,24(7):2120-2131. |
APA | Wang, Penghui,Qiao, Hongxia,Chen, Kefan,Li, Yuanke,&Feng, Qiong.(2020).Life Prediction and Long-Term Durability of Coated Steel Bars in Magnesium Oxychloride Concrete.KSCE Journal of Civil Engineering,24(7),2120-2131. |
MLA | Wang, Penghui,et al."Life Prediction and Long-Term Durability of Coated Steel Bars in Magnesium Oxychloride Concrete".KSCE Journal of Civil Engineering 24.7(2020):2120-2131. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Wang-2020-Life Predi(1932KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论