Effect mechanism of dilution on solidification crack in ENiCrFe-7 buffering layer of deposited metal | |
Yan, Yingjie1![]() ![]() ![]() | |
2020-07-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution
![]() |
ISSN | 0253360X |
卷号 | 41期号:7页码:12-17 |
摘要 | Larger size microcracks were found in the buffering layer when ENiCrFe-7 nickel-based welding material is used as filler metal to weld Q345B steel. Adopting optical microscope, scanning electron microscope and energy spectrometer were used to analyse the distribution, morphology, and precipitation of cracks and compared results with the the area where no crack occurs. The results show that cracks are only distributed in the buffering layer which adjacent to the base material, and the dilution rate, Fe content, and number of Nb-rich precipitates in the crack occurrence area are higher than those in the area where no crack occurs; The crack is typical solidification crack and precipitation phases rich in Nb and S elements exist on the crack surface; The low melting point phase rich in Nb and S is the main cause of solidification cracking of buffering layer. Copyright © 2020 Transactions of the China Welding Institution. All rights reserved. |
关键词 | Filler metals Microcracks Morphology Scanning electron microscopy Crack occurrences Effect mechanism Energy spectrometer Low-melting-point-phase Nb-rich precipitates Solidification cracking Solidification cracks Welding materials |
DOI | 10.12073/j.hjxb.20200202001 |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20204409408315 |
EI主题词 | Solidification |
EI分类号 | 538.2 Welding ; 802.3 Chemical Operations ; 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/150879 |
专题 | 材料科学与工程学院_特聘教授组 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.The State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Atlantic China Welding Consumables, INC., Zigong; 643000, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Yan, Yingjie,Zhang, Kaijia,Wang, Ruomeng,et al. Effect mechanism of dilution on solidification crack in ENiCrFe-7 buffering layer of deposited metal[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2020,41(7):12-17. |
APA | Yan, Yingjie,Zhang, Kaijia,Wang, Ruomeng,Jiang, Yong,Cao, Rui,&Chen, Jianhong.(2020).Effect mechanism of dilution on solidification crack in ENiCrFe-7 buffering layer of deposited metal.Hanjie Xuebao/Transactions of the China Welding Institution,41(7),12-17. |
MLA | Yan, Yingjie,et al."Effect mechanism of dilution on solidification crack in ENiCrFe-7 buffering layer of deposited metal".Hanjie Xuebao/Transactions of the China Welding Institution 41.7(2020):12-17. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论