Low-cycle fatigue test and life assessment of carbon structural steel GB Q235B butt joints and cruciform joints | |
Fang, Zhao1,2; Li, Aiqun1,3; Shen, Sheng1; Li, Wanrun1,4![]() | |
2019-02-01 | |
发表期刊 | Advances in Structural Engineering
![]() |
ISSN | 13694332 |
卷号 | 22期号:3页码:581-596 |
摘要 | Axial low-cycle fatigue tests are conducted on transverse butt joint specimens and cruciform joint specimens made of carbon structural steel GB Q235B. The effect of slip between the specimens and the grips of the test machine is considered by the proposal of a linear slip model. The cyclic softening properties are studied by observing the variation of stress amplitude with cycles. The cyclic stress–strain curve and the strain–life curve for both kinds of specimens are obtained based on the fatigue test data, and the corresponding coefficients are fitted. In order to verify the fatigue test results, finite element models of specimens are established and the corresponding fatigue life assessment is conducted using the local stress–strain approach and the equivalent structural stress approach, respectively. The results show that the effect of slip is unneglectable and the established linear slip model is reasonable. The two kinds of specimens both show a strain softening property, but cruciform joint specimens experience sudden falls of stress amplitude during the test due to the damage of welded lines; cruciform joint specimens show an either one-side failure mode or two-side failure mode while butt joint specimens only show a one-side failure mode; the two-side failure mode tends to lead to shorter fatigue life, so in the design of cruciform joint, such failure mode should be avoided. © The Author(s) 2018. |
关键词 | Building materials Butt welding Capillary flow Failure modes Fatigue testing Steel construction Steel testing Welds Butt joints Cruciform joints Fatigue assessments Low-cycle fatigue tests slip |
DOI | 10.1177/1369433218795292 |
收录类别 | EI ; SCIE |
语种 | 英语 |
WOS研究方向 | Construction & Building Technology ; Engineering |
WOS类目 | Construction & Building Technology ; Engineering, Civil |
WOS记录号 | WOS:000456529600002 |
出版者 | SAGE Publications Inc., United States |
EI入藏号 | 20190406421323 |
EI主题词 | Fatigue of materials |
EI分类号 | 538.2 Welding ; 538.2.1 Welding Processes ; 545.3 Steel ; 631.1 Fluid Flow, General ; 951 Materials Science |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/150637 |
专题 | 土木工程学院 |
通讯作者 | Li, Aiqun |
作者单位 | 1.Southeast Univ, Sch Civil Engn, Nanjing 210000, Jiangsu, Peoples R China; 2.Kyoto Univ, Grad Sch Engn, Kyoto, Japan; 3.Beijing Univ Civil Engn & Architecture, Beijing Adv Innovat Ctr Future Urban Design, Beijing, Peoples R China; 4.Lanzhou Univ Technol, Inst Earthquake Protect & Disaster Mitigat, Lanzhou, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Fang, Zhao,Li, Aiqun,Shen, Sheng,et al. Low-cycle fatigue test and life assessment of carbon structural steel GB Q235B butt joints and cruciform joints[J]. Advances in Structural Engineering,2019,22(3):581-596. |
APA | Fang, Zhao,Li, Aiqun,Shen, Sheng,&Li, Wanrun.(2019).Low-cycle fatigue test and life assessment of carbon structural steel GB Q235B butt joints and cruciform joints.Advances in Structural Engineering,22(3),581-596. |
MLA | Fang, Zhao,et al."Low-cycle fatigue test and life assessment of carbon structural steel GB Q235B butt joints and cruciform joints".Advances in Structural Engineering 22.3(2019):581-596. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论