Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing | |
Li, Chunyan1,2; Lu, Yu2; Li, Xinling2; Zhao, Zhenxiang2; Kou, Shengzhong1,2; Liaw, Peter K.3 | |
2021-10-15 | |
发表期刊 | JOURNAL OF NON-CRYSTALLINE SOLIDS |
ISSN | 0022-3093 |
卷号 | 570 |
摘要 | Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 (x=0.5, 0.75, 1) high-entropy alloys (HEAs) fabricated by copper mold suction casting were studied in this paper. The crystal structure of the alloy is composed of single-phase FCC solid solution, and the crystal structure does not change with the change of Cr content. The yield strength of as-cast alloys is below 200 MPa, and the elongation is above 50%. After cold-rolling and annealing, the strength and hardness of the alloy increase with the increase of Cr content. The comprehensive mechanical properties of the alloy with x=1 reach the best. The yield strength, tensile strength and elongation are 498 MPa, 770 MPa and 40%, respectively. The cubic texture of {001} 100 is the strongest texture of the specimen with x=0.5. The appropriate addition of Cr is beneficial to improve the corrosion resistance of the alloy. The alloy with x=0.75 has the best corrosion resistance in 0.5 mol/L H2SO4. The reduction of Cr content is advantageous to improve the soft magnetic properties of alloys, and Fe1.25CoCr0.5Ni1.25Al0.25 shows excellent magnetic properties. The Fe1.25CoCr0.5Ni1.25Al0.25 HEA, meanwhile, has good processability with the elongation over 50%. |
关键词 | High-entropy alloys Microstructures Mechanical properties Corrosion resistance Magnetic properties |
DOI | 10.1016/j.jnoncrysol.2021.121023 |
收录类别 | EI ; SCOPUS ; SCIE |
语种 | 英语 |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics ; Materials Science, Multidisciplinary |
WOS记录号 | WOS:000687330300001 |
出版者 | ELSEVIER |
EI入藏号 | 20212810635745 |
EI主题词 | Corrosion resistance |
EI分类号 | 531 Metallurgy and Metallography - 535.1.2 Rolling Mill Practice - 539.1 Metals Corrosion - 541.2 Aluminum Alloys - 543.1 Chromium and Alloys - 545.2 Iron Alloys - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 641.1 Thermodynamics - 701.2 Magnetism: Basic Concepts and Phenomena - 933.1.1 Crystal Lattice - 951 Materials Science |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/148922 |
专题 | 材料科学与工程学院 |
通讯作者 | Li, Chunyan |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Gansu, Peoples R China; 3.Univ Tennessee, Dept Mat Sci & Engn, Knoxville, TN 37996 USA |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 材料科学与工程学院 |
通讯作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 材料科学与工程学院 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Li, Chunyan,Lu, Yu,Li, Xinling,et al. Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS,2021,570. |
APA | Li, Chunyan,Lu, Yu,Li, Xinling,Zhao, Zhenxiang,Kou, Shengzhong,&Liaw, Peter K..(2021).Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing.JOURNAL OF NON-CRYSTALLINE SOLIDS,570. |
MLA | Li, Chunyan,et al."Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing".JOURNAL OF NON-CRYSTALLINE SOLIDS 570(2021). |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[Li, Chunyan]的文章 |
[Lu, Yu]的文章 |
[Li, Xinling]的文章 |
百度学术 |
百度学术中相似的文章 |
[Li, Chunyan]的文章 |
[Lu, Yu]的文章 |
[Li, Xinling]的文章 |
必应学术 |
必应学术中相似的文章 |
[Li, Chunyan]的文章 |
[Lu, Yu]的文章 |
[Li, Xinling]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论