Microstructure and mechanical properties of submerged arc welding filled with Ni wire dissimilar joints comprising SUS304 and Q245R | |
Zhang, Peng Xian; Zhao, Peng; Cui, Yan Quan | |
2014 | |
会议名称 | 2014 International Conference on Materials Science and Engineering Technology, MSET 2014 |
会议录名称 | Advanced Materials Research
![]() |
卷号 | 936 |
页码 | 1780-1785 |
会议日期 | June 28, 2014 - June 29, 2014 |
会议地点 | Shanghai, China |
出版者 | Trans Tech Publications Ltd |
摘要 | Aim at the issue that the bending crack is easy to generate inside dissimilar welded joint of low alloy steel and stainless steel, a new process of submerged arc welding filled with Ni wire is put forward. The influence mechanism of filling quantity of Ni wire to the joint of microstructure evolutions and mechanical properties is mainly explored based on the contrast test of non-filling Ni wire and three different filling speeds of Ni wire. The experiment results indicate that, the filling process of Ni wire supplies austenite forming element, and alters heat allocation process of molten pool. The filling quantity of Ni wire is the quantitative parameter, it is used to control the transition width between low alloy steel and weld metal, also to adjust the peak temperature and holding time at elevated temperature of molten pool. When the value of the filling quantity of Ni wire is determined, the problem of bending crack in the fusion zone of low alloy steel can be solved, and also the overheat damage can be eliminated. At the same time, the grains of weld metal and heat affected zone are refined. And on this basis the plasticity, toughness and microhardness of welded joint can be guaranteed. © (2014) Trans Tech Publications, Switzerland. |
关键词 | Cracks Engineering technology Filling Mechanical properties Microstructure Nickel Submerged arc welding Welding Welds Elevated temperature Influence mechanism Micro-structure evolutions Microstructure and mechanical properties Ni wires Peak temperatures Quantitative parameters Transition widths |
DOI | 10.4028/www.scientific.net/AMR.936.1780 |
收录类别 | EI |
语种 | 英语 |
EI入藏号 | 20142917947956 |
EI主题词 | Wire |
ISSN | 10226680 |
来源库 | Compendex |
分类代码 | 421 Strength of Building Materials; Mechanical Properties - 535.2 Metal Forming - 538.2 Welding - 538.2.1 Welding Processes - 548.1 Nickel - 691.2 Materials Handling Methods - 901 Engineering Profession - 902 Engineering Graphics; Engineering Standards; Patents - 933 Solid State Physics - 951 Materials Science |
引用统计 | 无
|
文献类型 | 会议论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/117286 |
专题 | 兰州理工大学 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Zhang, Peng Xian,Zhao, Peng,Cui, Yan Quan. Microstructure and mechanical properties of submerged arc welding filled with Ni wire dissimilar joints comprising SUS304 and Q245R[C]:Trans Tech Publications Ltd,2014:1780-1785. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论