Meso-damage evolution analysis of magnesium oxychloride cement concrete based on X-CT and grey-level co-occurrence matrix | |
Wang, Penghui1; Qiao, Hongxia1,2; Zhang, Yunsheng1,3; Li, Yuanke1; Feng, Qiong1; Chen, Kefan1 | |
2020-09-20 | |
发表期刊 | Construction and Building Materials |
ISSN | 09500618 |
卷号 | 255 |
摘要 | X-CT technology can be used to analyse the internal damage to concrete due to rust expansion. However, the original X-CT slice of the internal damage of the concrete can only be used to quantitatively analyse the internal damage in the specimen. The X-CT pictures of the concrete cannot deeply excavate the slight changes in the concrete specimens before and after damage due to rust expansion. As a texture feature analysis method, grey-level co-occurrence matrices (GLCM) have the ability to deeply mine the subtle grey-scale changes of original X-CT pictures. Therefore, this paper coupled X-CT and GLCM to analyse the internal damage in magnesium oxychloride cement concrete due to rust expansion. The four characteristic values of GLCM—contrast, correlation, energy and homogeneity—are used to reflect the internal concrete damage's evolution. The results show that there is a significant exponential relationship between the surface crack formation and the internal volume growth of the specimen. The contrast value gradually increases during the concrete damage process, while the correlation, energy and homogeneity values gradually decrease during this process, and these four eigenvalues all follow the normal distribution. By using these four characteristic values to analyse the reliability of concrete specimens, it is concluded that homogeneity can be better used to evaluate the internal damage of concrete specimens. The peak bandwidth of matrix in a color heat map decreases gradually and extends along the main diagonal of the matrix in the process of specimen damage that can be used to accurately reflect the damage to the concrete due to the rust expansion force. © 2020 Elsevier Ltd |
关键词 | Cements Eigenvalues and eigenfunctions Magnesium compounds Normal distribution Textures Characteristic value Co-occurrence-matrix Concrete specimens Grey level co-occurrence matrixes Internal damages Magnesium oxychloride cement Texture features X-CT technologies |
DOI | 10.1016/j.conbuildmat.2020.119373 |
收录类别 | EI |
语种 | 英语 |
出版者 | Elsevier Ltd |
EI入藏号 | 20201908614172 |
EI主题词 | Concretes |
来源库 | Compendex |
分类代码 | 412 Concrete - 412.1 Cement - 922.1 Probability Theory |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/115327 |
专题 | 土木工程学院 材料科学与工程学院 |
作者单位 | 1.School of Civil Engineering, Lanzhou University of Technology, Lanzhou Gansu, China; 2.Key Laboratory of Disaster Prevention and Mitigation in Civil Engineering of Gansu Province, Lanzhou University of Technology, Lanzhou, China; 3.School of Materials Science and Engineering, Southeast University, Nanjing, China |
第一作者单位 | 土木工程学院 |
第一作者的第一单位 | 土木工程学院 |
推荐引用方式 GB/T 7714 | Wang, Penghui,Qiao, Hongxia,Zhang, Yunsheng,et al. Meso-damage evolution analysis of magnesium oxychloride cement concrete based on X-CT and grey-level co-occurrence matrix[J]. Construction and Building Materials,2020,255. |
APA | Wang, Penghui,Qiao, Hongxia,Zhang, Yunsheng,Li, Yuanke,Feng, Qiong,&Chen, Kefan.(2020).Meso-damage evolution analysis of magnesium oxychloride cement concrete based on X-CT and grey-level co-occurrence matrix.Construction and Building Materials,255. |
MLA | Wang, Penghui,et al."Meso-damage evolution analysis of magnesium oxychloride cement concrete based on X-CT and grey-level co-occurrence matrix".Construction and Building Materials 255(2020). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论