Analysis of impact toughness variation for flat position multi-pass weld joint | |
Yuan, Junjun1; Chan, Zhishan1; Cao, Rui1![]() | |
2017-05-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution
![]() |
ISSN | 0253360X |
卷号 | 38期号:5页码:100-103 |
摘要 | A multi-pass weld metal in flat position was studied, which was welded by a flux cored wire used in X70 pipeline. Analysis included observation of the fracture surfaces to determine initiation location (optical and scanning electron microscopy) and metallographic examination of the weld microstructures. It was found that the position of impact specimen is different, which will cause different impact energy; the proportion of the columnar crystal or coarse crystal area,which was near the position of impact specimen notch root, was a main reason for the impact toughness variation but is not the main reason of low values. The weld defects and coarse grain were the main reason for the variation and low values of impact toughness. When the impact energy is 54.2 J, the impact sample was cleavage fracture. Crack source were welding defects such as inclusions, the defects of incomplete fusion and so on, and the nearer the position of these defects to the notch, the smaller the impact energy. © 2017, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
关键词 | Defects Fracture toughness Scanning electron microscopy Submerged melt welding Cleavage fracture Columnar crystals Fracture surfaces Metallographic examination Multi-pass weld metal Toughness variations Variation Weld microstructures |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20173704160727 |
EI主题词 | Welds |
EI分类号 | 538.2 Welding - 538.2.1 Welding Processes - 933.1 Crystalline Solids - 951 Materials Science |
来源库 | Compendex |
分类代码 | 538.2 Welding - 538.2.1 Welding Processes - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/114562 |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Hobart Brothers Company, An ITW Welding Company, Troy; 45373, United States |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Yuan, Junjun,Chan, Zhishan,Cao, Rui,et al. Analysis of impact toughness variation for flat position multi-pass weld joint[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2017,38(5):100-103. |
APA | Yuan, Junjun,Chan, Zhishan,Cao, Rui,Mao, Gaojun,&Xiao, George.(2017).Analysis of impact toughness variation for flat position multi-pass weld joint.Hanjie Xuebao/Transactions of the China Welding Institution,38(5),100-103. |
MLA | Yuan, Junjun,et al."Analysis of impact toughness variation for flat position multi-pass weld joint".Hanjie Xuebao/Transactions of the China Welding Institution 38.5(2017):100-103. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论