Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel | |
Yang, Guirong1![]() ![]() | |
2019-02-25 | |
发表期刊 | Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research
![]() |
ISSN | 10053093 |
卷号 | 33期号:2页码:87-94 |
摘要 | Ni+WC composite cladding was prepared on the surface of 45 # steel by vacuum cladding technology. The formation mechanism of nickel-based composite coating was investigated by intermittently sampling. The results show that a Ni-based composite cladding with metallurgical fusion to the matrix and uniform distribution of WC hard particles is obtained on the surface of 45 steel. The entire cladding consists of a 4 mm thick composite layer, a 1 mm thick transition layer, a 20 μm thick diffusion fused zone, and a 250 μm thick diffusion affected zone. The composite layer composes of WC and W-rich multiphase carbide formed after decomposition, surrounded by Ni particles; The main phase constituents of the composite cladding layer include γ- Ni solid solution, Cr7C3, Ni2.9Cr0.7Fe0.36, Cr23C6, Ni3Fe, Ni3Si, Ni3B, W2C and C. The vacuum cladding process mainly includes the formation of a micro-sintered neck between the particles in the heating stage before the Ni-based alloy particles reach its melting point, and the melting of the Ni-based alloy particles at the beginning stage of its melting point and the third stages of fusion diffusion in the heat preservation stage and position adjustment of the WC particle within micro-area. © All right reserved. |
关键词 | Cladding (coating) Composite coatings Composite materials Diffusion Melting point Nickel alloys Nickel coatings Sintered carbides Steel metallurgy Ternary alloys Diffusion-affected zone Formation mechanism Heat preservation Nickel-based composites Phase constituent Thick composites Transition layers Uniform distribution |
DOI | 10.11901/1005.3093.2018.510 |
收录类别 | EI |
语种 | 中文 |
出版者 | Chinese Journal of Materials Research |
EI入藏号 | 20192006915099 |
EI主题词 | Nickel steel |
EI分类号 | 531.1 Metallurgy - 548.1 Nickel - 548.2 Nickel Alloys - 804.2 Inorganic Compounds - 813.2 Coating Materials - 931.2 Physical Properties of Gases, Liquids and Solids - 951 Materials Science |
来源库 | Compendex |
分类代码 | 531.1 Metallurgy - 548.2 Nickel Alloys - 804.2 Inorganic Compounds - 813.2 Coating Materials - 931.2 Physical Properties of Gases, Liquids and Solids - 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/114105 |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Lanpec Technologies Co. Ltd., Lanzhou; 730070, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Yang, Guirong,Gao, Dawen,Song, Wenming,et al. Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel[J]. Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,2019,33(2):87-94. |
APA | Yang, Guirong,Gao, Dawen,Song, Wenming,Zhang, Yufu,&Ma, Ying.(2019).Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel.Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,33(2),87-94. |
MLA | Yang, Guirong,et al."Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel".Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research 33.2(2019):87-94. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论