Effect of mechanical attrition on microstructure and properties of electroless-plated Ni-P coatings on zinc alloy | |
Li, Ya-Min; Wang, Li-Bo; Liu, Hong-Jun | |
2013-03-01 | |
发表期刊 | Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment |
ISSN | 10096264 |
卷号 | 34期号:3页码:154-159 |
摘要 | A mechanically assisted electroless (MAE) plating technique was applied in the process of conventional electroless (CE) Ni-P plating on a zinc alloy by stirring the plating solution containing glass balls. Then the effect of the mechanical attrition on microstructure and properties of electroless-plated Ni-P coatings was studied by means of XRD, SEM, AFM, micro-hardness test and electrochemical experiments. The results show that the amorphous structure is obtained and the content of phosphorus decreases for the MAE plated coating. And the MAE plated coating shows smooth surface morphology, pores-free and more compactness. Therefore, the hardness and corrosion resistance of the novel coatings are considerably improved compared with that of the CE-plated Ni-P coatings. In MAE plating process, the activation energy of reaction is decreased, but the deposition rate of electroless palting is decreased too. |
关键词 | Activation energy Corrosion resistance Electroless plating Hardness Microstructure Nickel Structure (composition) Zinc alloys Amorphous structures Electrochemical experiments Hardness and corrosion Mechanical attrition Microhardness tests Microstructure and properties Ni-P coating Plating solutions |
收录类别 | EI |
语种 | 中文 |
出版者 | Editorial Office of Transactions of Materials, 18 Xueqing Road, Beijing, 100083, China |
EI入藏号 | 20131716238422 |
EI主题词 | Coatings |
EI分类号 | 539 Metals Corrosion and Protection ; Metal Plating - 546.3 Zinc and Alloys - 548.1 Nickel - 801.4 Physical Chemistry - 951 Materials Science |
来源库 | Compendex |
分类代码 | 539 Metals Corrosion and Protection; Metal Plating - 546.3 Zinc and Alloys - 548.1 Nickel - 801.4 Physical Chemistry - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/113256 |
专题 | 材料科学与工程学院 国际教育学院 |
作者单位 | Key Laboratory of Non-Ferrous Metal Alloys and Processing, the Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Li, Ya-Min,Wang, Li-Bo,Liu, Hong-Jun. Effect of mechanical attrition on microstructure and properties of electroless-plated Ni-P coatings on zinc alloy[J]. Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,2013,34(3):154-159. |
APA | Li, Ya-Min,Wang, Li-Bo,&Liu, Hong-Jun.(2013).Effect of mechanical attrition on microstructure and properties of electroless-plated Ni-P coatings on zinc alloy.Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,34(3),154-159. |
MLA | Li, Ya-Min,et al."Effect of mechanical attrition on microstructure and properties of electroless-plated Ni-P coatings on zinc alloy".Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment 34.3(2013):154-159. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论