Effects of Si and Mg on mechanical properties of aluminum-steel welded-brazed joint | |
Huang, Jiankang1; Li, Jie1; Shen, Limin2; Shi, Yu1; Gu, Yufen1; Fan, Ding2 | |
2016-08-25 | |
发表期刊 | Hanjie Xuebao/Transactions of the China Welding Institution |
ISSN | 0253360X |
卷号 | 37期号:8页码:96-100 |
摘要 | Dissimilar metals of 5052 aluminum alloy and galvanized steel were joined with lap joint by pulsed double electrode gas metal arc welding-brazing with ER4043 filler metal and ER5356 filler metal, respectively. The interfacial microstructures, fracture behavior and fracture morphologies of the joints were analyzed by scanning electron microscopy, energy dispersive spectroscopy and X-Ray diffraction. The results show that wetting angle of weld with Al-Mg filler metal is larger than that with Al-Si filler metal. Si atoms change the shape of intermetallic compounds and inhibit the formation of Fe2Al5 intermetallic compound. The results of tensile tests show that the welded joints with Al-Mg filler metal mainly fracture along the interface between the intermetallic layer and the steel, and the fracture mode of the joints is brittle fracture. The welded joints with Al-Si filler metal mainly fracture in the fusion zone of aluminum alloy, and the fracture mode of the joints mainly is ductile fracture, but has the trace of brittle fracture. Hardness of joints with Al-Si filler metal was determined, the results show that the hardness of aluminum heat affect zone is obviously lower than that of the other zone, which leads to the joints with Al-Si filler metal failure in aluminum fusion zone. © 2016, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
关键词 | Binary alloys Brazing Brittle fracture Dissimilar metals Ductile fracture Energy dispersive spectroscopy Filler metals Fillers Fracture mechanics Galvanized metal Galvanizing Gas metal arc welding Gas welding Hardness Intermetallics Iron alloys Magnesium Metal testing Metals Microstructure Scanning electron microscopy Silicon Tensile testing Trace elements Welded steel structures Welds 5052 aluminum alloy Aluminum steel Double electrodes Fracture morphology Galvanized steels Interfacial microstructure Intermetallic layer Microstructures and properties |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20163602773071 |
EI主题词 | Aluminum alloys |
EI分类号 | 531 Metallurgy and Metallography - 538 Welding and Bonding - 539.3 Metal Plating - 541.1 Aluminum - 541.2 Aluminum Alloys - 549.2 Alkaline Earth Metals - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 931.1 Mechanics - 951 Materials Science |
来源库 | Compendex |
分类代码 | 531 Metallurgy and Metallography - 531.1 Metallurgy - 538 Welding and Bonding - 539.3 Metal Plating - 541.2 Aluminum Alloys - 545.2 Iron Alloys - 549.2 Alkaline Earth Metals - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 931.1 Mechanics - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/113001 |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Great Wall Motor Company Limited, Baoding; 071000, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Huang, Jiankang,Li, Jie,Shen, Limin,et al. Effects of Si and Mg on mechanical properties of aluminum-steel welded-brazed joint[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2016,37(8):96-100. |
APA | Huang, Jiankang,Li, Jie,Shen, Limin,Shi, Yu,Gu, Yufen,&Fan, Ding.(2016).Effects of Si and Mg on mechanical properties of aluminum-steel welded-brazed joint.Hanjie Xuebao/Transactions of the China Welding Institution,37(8),96-100. |
MLA | Huang, Jiankang,et al."Effects of Si and Mg on mechanical properties of aluminum-steel welded-brazed joint".Hanjie Xuebao/Transactions of the China Welding Institution 37.8(2016):96-100. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论