Effects of T6 treatment on microstructure and properties of thixoformed Mg2Sip/AM60B composite | |
Cheng, Fa-Liang1; Chen, Ti-Jun1,2![]() | |
2015-10-25 | |
发表期刊 | Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
![]() |
ISSN | 10096264 |
卷号 | 36期号:10页码:32-38 |
摘要 | The effects of T6 treatment (430 , 6 h+215 , 2 h, air cooling) on microstructure and mechanical properties of thixoformed Mg2Sip/AM60B composite were investigated. The results indicate that the hard and brittle β (Mg17Al12) phase which distributed both along the grain boundary and within the grain is almost dissolved after T4 treatment (430 ×6 h, water cooling). The tensile properties of the composite remarkably improved due to the basic disappearance of β phase harmfulness, increased solid solution strengthening and composition homogenization. However, the hardness decreases significantly. After T6 treatment, the discontinuous precipitation of β phase dispersively distributes at grain boundary and interface of Mg2Si/α-Mg. According to the fine and dispersed distribution of β phase, the pinning effect at grain boundary increases remarkably and lead to the increasing of ultimate tensile strength (UTS) and hardness of the composite. The elongation slightly decreases. No obvious continuous precipitations of β phase can be found at the present T6 treatment. The optimum T6 heat treatment for thixoformed Mg2Sip/AM60B composite is (430 , 6 h+215 , 2 h) and the tensile properties are up to UTS of 290 MPa and elongation of 14.3%, increased by 40.10% and 83.06% respectively compared with those of the as-thixoformed composite. In general, the fracture regime changes from intergranular of as-thixoformed composite in turn to a mixture of intergranular and transgranular form of T4 treated and transgranular regime of T6 treated composite. ©, 2015, Editorial Office of Transactions of Materials and Heat Treatment. All right reserved. |
关键词 | Composite materials Grain boundaries Hardness Mechanical properties Microstructure Silicon Stress corrosion cracking Textures Continuous precipitation Discontinuous precipitation Microstructure and mechanical properties Microstructure and properties Solid solution strengthening T6 treatment Thixo-forming Ultimate tensile strength |
收录类别 | EI |
语种 | 中文 |
出版者 | Editorial Office of Transactions of Materials and Heat Treatment |
EI入藏号 | 20154801606066 |
EI主题词 | Tensile strength |
EI分类号 | 539.1 Metals Corrosion - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 951 Materials Science |
来源库 | Compendex |
分类代码 | 539.1 Metals Corrosion - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/112819 |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou, China; 2.Key Laboratory of Non-ferrous Metal Alloys and Processing of the Ministry of Education, Lanzhou University of Technology, Lanzhou, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Cheng, Fa-Liang,Chen, Ti-Jun,Zhang, Su-Qing,et al. Effects of T6 treatment on microstructure and properties of thixoformed Mg2Sip/AM60B composite[J]. Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,2015,36(10):32-38. |
APA | Cheng, Fa-Liang,Chen, Ti-Jun,Zhang, Su-Qing,&Qi, Ye-Si.(2015).Effects of T6 treatment on microstructure and properties of thixoformed Mg2Sip/AM60B composite.Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,36(10),32-38. |
MLA | Cheng, Fa-Liang,et al."Effects of T6 treatment on microstructure and properties of thixoformed Mg2Sip/AM60B composite".Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment 36.10(2015):32-38. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论