摘要 | A new activating TIG welding process, gas transfer flux activating TIG (GTFA-TIG) welding, is proposed for welding aluminum alloy by changing the introduction method of active elements. In this process, a flux is transferred to shielding gas through an automatic powder feeder, and the shielding gas carries the active elements into the welding arc and weld pool. In this way, the welding arc is contracted, and the flow pattern in the weld pool is changed, finally, the weld depth increases. Without coating the flux, the automation of welding process is realized. Compared to the conventional AC TIG welding, the effects of fluxes on the weld shape, tensile property and defects of GTFA-TIG welding with eight kinds of single-component fluxes were investigated. It proves that most of halide and oxide fluxes can improve the weld depth up to 2.5-3.0 times of that of traditional TIG welding, while the effect of Te flux is less effective. The tensile strength of the joint with V2O5 flux is close to that of base metal, but it is lower than that of base metal when using MnCl2 and AlF3 fluxes. The X-ray detection of defects shows that the welds with V2O5, MnCl2 and AlF3 fluxes are assessed as grade I, while that with Te flux is grade III. |
关键词 | Aluminum alloys Aluminum compounds Chemical activation Chlorine compounds Defects Flow patterns Gas welding Inert gas welding Laser beam welding Manganese compounds Shielding Tellurium Tensile strength Vanadium pentoxide Welds Activating flux Activating TIG welding Active elements Powder feeder Single components TIG-welding Welding process X-ray detections |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20141017431007 |
EI主题词 | Fluxes |
EI分类号 | 538.2 Welding - 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 631.1 Fluid Flow, General - 804 Chemical Products Generally - 951 Materials Science |
来源库 | Compendex |
分类代码 | 538.2 Welding - 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 631.1 Fluid Flow, General - 804 Chemical Products Generally - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/112683 |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 机电工程学院 |
作者单位 | 1.State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2.Key Laboratory of Non-ferrous Metal Alloys, Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 兰州理工大学 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Huang, Yong,Li, Tao,Wang, Yanlei. Gas transfer flux activating TIG welding process for aluminum alloy[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2014,35(1):101-104. |
APA | Huang, Yong,Li, Tao,&Wang, Yanlei.(2014).Gas transfer flux activating TIG welding process for aluminum alloy.Hanjie Xuebao/Transactions of the China Welding Institution,35(1),101-104. |
MLA | Huang, Yong,et al."Gas transfer flux activating TIG welding process for aluminum alloy".Hanjie Xuebao/Transactions of the China Welding Institution 35.1(2014):101-104. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论