摘要 | FSSW without keyhole of Al6061 and DP600 zinc-coated steel was carried out by using the equipment designed by our team (top steel sheet-bottom Al sheet). Using scanning electron microscope, energy spectrometer and tensile test on the microstructure and mechanical properties of joint were studied. The results showed that the mixing head speed was 1200 r/min, the preheating time was 6 s and stirring needle length was 3.2 mm and joint shear resistance reached 11.2 kN. The surface of joint was smoothly without keyhole. Welding joint was composed of the stir zone and the diffusion zone, stir zone to hook shape the distribution of embedded steel in the aluminum matrix and finally form strong mechanical connection. The diffusion zone of aluminum and steel's connection depended on the interfacial intermetallic compounds. Connection mode was metallurgical combination. The fracture of welding joint's position was in between of the interface layer and the aluminum substrate. The distribution of river-shaped fracture was cleavage steps, so the mode of fracture belonged to brittle fracture. ©, 2015, Harbin Research Institute of Welding. All right reserved. |
关键词 | Aluminum coatings Fracture Friction stir welding Mechanical properties Microstructure Scanning electron microscopy Spot welding Tensile testing Zinc coatings Al-alloy Friction stir spot welding FSSW without keyhole Interfacial intermetallics Mechanical connections Metallurgical combinations Microstructure and mechanical properties Orthogonal test |
收录类别 | EI |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
EI入藏号 | 20151400699847 |
EI主题词 | Aluminum alloys |
EI分类号 | 538.2.1 Welding Processes - 541.1 Aluminum - 541.2 Aluminum Alloys - 813.2 Coating Materials - 951 Materials Science |
来源库 | Compendex |
分类代码 | 538.2.1 Welding Processes - 541.2 Aluminum Alloys - 813.2 Coating Materials - 951 Materials Science |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/112349 |
专题 | 材料科学与工程学院 |
作者单位 | State Key Laboratory of Ministry of Non-Ferrous Metals Advanced Processing and Reuse, Lanzhou University of Technology, Lanzhou; 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Wang, Xijing,Zhang, Yazhou,Zhang, Zhongke,et al. Welding analyses of friction stir spot welding without keyhole between aluminum alloy and zinc-coated steel[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2015,36(1):1-4. |
APA | Wang, Xijing,Zhang, Yazhou,Zhang, Zhongke,&Sun, Xuemin.(2015).Welding analyses of friction stir spot welding without keyhole between aluminum alloy and zinc-coated steel.Hanjie Xuebao/Transactions of the China Welding Institution,36(1),1-4. |
MLA | Wang, Xijing,et al."Welding analyses of friction stir spot welding without keyhole between aluminum alloy and zinc-coated steel".Hanjie Xuebao/Transactions of the China Welding Institution 36.1(2015):1-4. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论