Degree of ordering of Fe3 (Si, Al) powders prepared by high energy ball milling and annealing | |
Jia, Jian-Gang1![]() ![]() ![]() ![]() ![]() | |
2008-04-01 | |
发表期刊 | Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
![]() |
ISSN | 10096264 |
卷号 | 29期号:2页码:36-39 |
摘要 | The ball milling process of 3Fe/xSi/(1-x) Al (x = 0.75, 0.5, 0.25) powder mixtures were studied by Fritsch Pulversitte 5 ball mill, scanning electron microscopy, and X-ray diffraction. Powders milled for 1h and 5h were annealed at 860°C for 4h and the phase constitutions of the annealed powders were investigated as well. The long range order parameter (LRO) was used to evaluate the degree of ordering of the ordered phase. The findings indicated that Fe (Si, Al) solid solutions can be produced after milling for more than 5h. The crystallite size of the solid solution milled for 5h is about 20 nm. The ordered phase of 3Fe/xSi/(1-x) Al (x = 0.75, 0.5, 0.25) powder mixtures milled for 5h and annealed at 860°C for 4h are Al0.3Fe3Si0.7, Al0.5Fe3Si0.5 and Al0.7Fe3Si0.3. The degrees of ordering of the three ordered phases are 0.7906, 0.6888 and 0.7302, respectively. |
关键词 | Aluminum alloys Annealing Iron alloys Phase structure Powders Silicon alloys Solid solutions Degree of ordering High energy ball milling Iron aluminum alloys Iron silicon alloys Long range order parameter (LRO) |
收录类别 | EI |
语种 | 中文 |
出版者 | Editorial Office of Transactions of Materials, 18 Xueqing Road, Beijing, 100083, China |
EI入藏号 | 20082311303095 |
EI主题词 | Ball milling |
EI分类号 | 933 Solid State Physics - 931.2 Physical Properties of Gases, Liquids and Solids - 802.3 Chemical Operations - 545.3 Steel - 545.2 Iron Alloys - 541.2 Aluminum Alloys - 537.1 Heat Treatment Processes |
来源库 | Compendex |
分类代码 | 933 Solid State Physics - 931.2 Physical Properties of Gases, Liquids and Solids - 802.3 Chemical Operations - 545.3 Steel - 545.2 Iron Alloys - 541.2 Aluminum Alloys - 537.1 Heat Treatment Processes |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/111920 |
专题 | 材料科学与工程学院 外国语学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.State Key Laboratory of Gansu Advanced Non-Ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Jia, Jian-Gang,Ma, Qin,Lu, Jin-Jun,et al. Degree of ordering of Fe3 (Si, Al) powders prepared by high energy ball milling and annealing[J]. Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,2008,29(2):36-39. |
APA | Jia, Jian-Gang,Ma, Qin,Lu, Jin-Jun,Zhou, Qi,Ji, Gen-Shun,&Guo, Tie-Ming.(2008).Degree of ordering of Fe3 (Si, Al) powders prepared by high energy ball milling and annealing.Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,29(2),36-39. |
MLA | Jia, Jian-Gang,et al."Degree of ordering of Fe3 (Si, Al) powders prepared by high energy ball milling and annealing".Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment 29.2(2008):36-39. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论