Fabrication of Ni-based alloy composite substrate with high cube texture using hot isostatic presses method | |
Qiu, Huo-Qin1; Suo, Hong-Li1; Kou, Sheng-Zhong1,2; Ma, Lin1; Tian, Hui1; Liu, Min1; Yuan, Dong-Mei1; Wang, Ying-Xia1 | |
2011-07-01 | |
发表期刊 | Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals |
ISSN | 10040609 |
卷号 | 21期号:7页码:1632-1638 |
摘要 | A tri-layer composite alloy ingot was fabricated by hot isostatic presses (HIP) method, in which the outer layer is Ni-5%W (Ni5W, mole fraction) alloy and the inner layer is Ni-12%W (Ni12W, mole fraction) alloy. The composite ingot was cold-rolled using the process of rolling assisted biaxially textured substrate (RABiTSTM) technology and annealed to obtain the Ni5W/Ni12W/Ni5W composite substrate with high cube texture. The cold rolling and the recrystallization textures on the surface of the as-obtained composite substrate were studied systematically by X-ray and EBSD measurements. The results show that a strong deformation copper-type texture is obtained in the cold rolled composite substrate, and a sharp cube texture is formed on the surface of Ni5W/Ni12W/Ni5W composite substrate after a recrystallization annealing process. The percentage of the cube orientated grain within a misorientation angle of 10° is as high as 99.1%, which is in the same level as that of the commercial Ni5W tape. |
关键词 | Binary alloys Cold rolling Fabrication Geometry Hot isostatic pressing Ingots Metal cladding Nickel alloys Presses (machine tools) Recrystallization (metallurgy) Sintering Substrates Superconducting films Textures Composite substrate Copper type texture Cube texture Misorientation angle Recrystallization texture Recrystallization-annealing Rolling assisted biaxially textured substrates Sharp cube textures |
收录类别 | EI |
语种 | 中文 |
出版者 | Central South University of Technology |
EI入藏号 | 20113414261132 |
EI主题词 | Tungsten alloys |
EI分类号 | 531.1 Metallurgy - 534.2 Foundry Practice - 535.1.2 Rolling Mill Practice - 543.5 Tungsten and Alloys - 548.2 Nickel Alloys - 603.1 Machine Tools, General - 708.3 Superconducting Materials - 921 Mathematics |
来源库 | Compendex |
分类代码 | 531.1 Metallurgy - 534.2 Foundry Practice - 535.1.2 Rolling Mill Practice - 543.5 Tungsten and Alloys - 548.2 Nickel Alloys - 603.1 Machine Tools, General - 708.3 Superconducting Materials - 921 Mathematics |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/111674 |
专题 | 材料科学与工程学院 |
作者单位 | 1.College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China; 2.College of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Qiu, Huo-Qin,Suo, Hong-Li,Kou, Sheng-Zhong,et al. Fabrication of Ni-based alloy composite substrate with high cube texture using hot isostatic presses method[J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,2011,21(7):1632-1638. |
APA | Qiu, Huo-Qin.,Suo, Hong-Li.,Kou, Sheng-Zhong.,Ma, Lin.,Tian, Hui.,...&Wang, Ying-Xia.(2011).Fabrication of Ni-based alloy composite substrate with high cube texture using hot isostatic presses method.Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,21(7),1632-1638. |
MLA | Qiu, Huo-Qin,et al."Fabrication of Ni-based alloy composite substrate with high cube texture using hot isostatic presses method".Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals 21.7(2011):1632-1638. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论