题名 | M:MgAl2O4(M=Mn,Cr)超细粉体的制备及发光性能的研究 |
作者 | 夏心俊 |
学位类型 | 硕士 |
导师 | 阎峰云 |
答辩日期 | 2014 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料学 |
关键词 | 共沉淀 镁铝尖晶石 Mn2+离子 Cr3+离子 发光性能 |
摘要 | 本文采用化学共沉淀法合成纯净尖晶石MgAl2O4超细粉体前驱体,研究了改性剂的加入和不同干燥方法的使用对粉体的影响。最终确定采用沉淀-共沸蒸馏法同时添加改性剂的方案合成前驱体,经过研磨,1150 ℃下成功制备出高质量纯净尖晶石MgAl2O4超细粉体。采用该工艺流程合成Mn2+/Cr3+单掺和Mn2+、Cr3+双掺尖晶石MgAl2O4超细粉体,对合成粉体的发光性能进行了研究。 |
其他摘要 | In this paper, the precursor of pure spinel MgAl2O4 ultrafine powder was synthesized by chemical co-precipitation method, and the effect of the addition of modifier and the use of different drying methods on the powder was studied.In the end, the precursor was prepared by precipitation azeotropic distillation method and adding modifier at the same time, and then the high quality pure spinel MgAl2O4 ultrafine powder was successfully prepared by grinding and 1150 degrees celsius.The Mn2+/Cr3+ single doped Mn2+ and Cr3+ double doped spinel MgAl2O4 ultrafine powders were synthesized by the process, and the luminescent properties of the powders were studied. |
页数 | 61 |
语种 | 中文 |
学号 | 142080502044 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/102927 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 夏心俊. M:MgAl2O4(M=Mn,Cr)超细粉体的制备及发光性能的研究[D]. 兰州理工大学,2014. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[夏心俊]的文章 |
百度学术 |
百度学术中相似的文章 |
[夏心俊]的文章 |
必应学术 |
必应学术中相似的文章 |
[夏心俊]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论