题名 | 316L不锈钢表面超音速火焰喷涂Ni60-CeO2复合涂层组织与性能研究 |
作者 | 陈威 |
学位类型 | 硕士 |
导师 | 胡勇 |
答辩日期 | 2014 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料加工工程 |
关键词 | 机械球磨 纳米CeO2 超音速火焰喷涂 摩擦磨损 热腐蚀 |
摘要 | 利用SEM、XRD以及激光粒度分析仪对复合粉末进行表征,结果表明:机械球磨工艺能够制备出适合超音速火焰喷涂的Ni60-CeO2复合粉末颗粒,当球磨时间为10h时,纳米CeO2颗粒均匀弥散地分布在Ni60颗粒上,并呈理想的单分散状态,晶粒尺寸为27.9nm,微观应变为0.32%,粉末形状呈椭球形,经过过筛后即可用于超音速火焰喷涂。 |
其他摘要 | The Ni60-CeO2 nanocomposite powder were investigated by scanning electron microscopy (SEM),X-ray diffraction (XRD),laser scattering for the particle size analysis,results show that the Ni60-CeO2 nanocomposite powder which is made by high-energy ball milling is suitable for the HVOF,After milled for 10h,the CeO2 nanoparticles are homogeneously distributed on the surface of Ni60 matrix,the average grain size and microstrain of the nanocomposite powder shape is ellipsoid and eventually stabilized, after sieved,it can be used for the HVOF. |
页数 | 65 |
语种 | 中文 |
学号 | 142080503030 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/102925 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 陈威. 316L不锈钢表面超音速火焰喷涂Ni60-CeO2复合涂层组织与性能研究[D]. 兰州理工大学,2014. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[陈威]的文章 |
百度学术 |
百度学术中相似的文章 |
[陈威]的文章 |
必应学术 |
必应学术中相似的文章 |
[陈威]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论