| 题名 | 不锈钢气体输送活性TIG焊方法研究 |
| 作者 | 姚宇航 |
| 学位类型 | 硕士 |
| 导师 | 黄勇 ; 张建晓 |
| 答辩日期 | 2012 |
| 学位授予单位 | 兰州理工大学 |
| 学位名称 | 工程硕士 |
| 学位专业 | 材料工程 |
| 关键词 | 不锈钢 GTFA-TIG焊 配方开发 工业应用 |
| 摘要 | 采用304不锈钢为试验板材，进行单组元焊接试验，分析不同种类活性剂对焊缝影响。对比普通TIG焊与GTFA-TIG焊电弧形貌，电压和高温亮白区宽度，不锈钢GTFA-TIG焊电弧电压升高，电弧有明显的收缩现象，卤化物电弧收缩强于氧化物。证明了电弧收缩可深化不锈钢GTFA-TIG焊缝熔深，卤化物增加不锈钢GTFA-TIG焊缝熔深的主要机理是收缩电弧。 |
| 其他摘要 | The effect of different fluxes on welding was analyzed by using SUS304 stainless steel as experiment plat.The comparisons of arc morphology,voltage and width of bright area of high temperature between common TIG and GTFA-TIG welding simplify that,in GTFA-TIG welding,there is an increase in arc voltage and has a significant arc shrink,at the same time,halide arc constriction is stronger than oxides.All of these results proved that,arc constriction can deepen weld depth of stainless steel by GTFA-TIG welding.The main mechanism of halide increase GTFA-TIG weld depth in stainless steel is arc constriction. |
| 页数 | 67 |
| 语种 | 中文 |
| 学号 | 122085204004 |
| 文献类型 | 学位论文 |
| 条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/102326 |
| 专题 | 兰州理工大学 |
| 作者单位 | 兰州理工大学 |
| 第一作者单位 | 兰州理工大学 |
| 推荐引用方式 GB/T 7714 | 姚宇航. 不锈钢气体输送活性TIG焊方法研究[D]. 兰州理工大学,2012. |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 查看访问统计 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [姚宇航]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [姚宇航]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [姚宇航]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论