| 题名 | 纯镁低温电解渗硫表面改性技术的研究 |
| 作者 | 邹荣
|
| 学位类型 | 硕士 |
| 导师 | 马颖 |
| 答辩日期 | 2012 |
| 学位授予单位 | 兰州理工大学 |
| 学位名称 | 工学硕士 |
| 学位专业 | 材料加工工程 |
| 关键词 | 纯镁 低温电解渗硫 正交试验 盐浴体系 水溶液体系 |
| 摘要 | 本课题实验采用低温电解渗硫技术，采用不同制备工艺条件，在硫氰酸盐（盐浴）和硫代硫酸钠（水溶液）两种体系中，在纯镁表面制备硫化物改性层。通过对改性层厚度、表面形貌、截面形貌、成分、耐蚀性、摩擦磨损性进行检测分析，验证了试样经处理后，表面形成了一定厚度的渗硫改性层，耐蚀性、耐磨性均得到提高，对纯镁基材起到了防护作用。并利用正交试验法，分别确定两种电解液体系中的最佳工艺参数搭配。 |
| 其他摘要 | This study have used the low-temperature electrolytic sulphuring technology under the different process conditions. The sulphide film have been prepared on the surface of pure magnesium in the thiocyanate and sodium thiosulfate solution system. The thickness, surface morphology, cross-section morphology, component, corrcsion resistance and wear resisitance of modified layer on the surface were studied and concluded that sulfurizing modified layer with a certain thickness were formed on the surface of the treated samples. The corrosion resistance and wear resistance were improved, and the pure magnesium substrate has been effectively protected. Moreover, the optimum technology parameters have been determined by the orthogonal experimental method in the two electrolyte system. |
| 页数 | 69 |
| 语种 | 中文 |
| 学号 | 122080503104 |
| 文献类型 | 学位论文 |
| 条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/101950 |
| 专题 | 马克思主义学院 |
| 作者单位 | 兰州理工大学 |
| 第一作者单位 | 兰州理工大学 |
| 推荐引用方式 GB/T 7714 | 邹荣. 纯镁低温电解渗硫表面改性技术的研究[D]. 兰州理工大学,2012. |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 查看访问统计 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [邹荣]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [邹荣]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [邹荣]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论