题名 | 铝合金7055搅拌摩擦对接焊接头微观组织与力学性能 |
作者 | 霍仁杰 |
学位类型 | 硕士 |
导师 | 金玉花 |
答辩日期 | 2012 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料加工工程 |
关键词 | 搅拌摩擦焊 7055铝合金 微观组织 力学性能 断裂特征 |
摘要 | 采用搅拌摩擦焊对5mm板厚铝合金7055进行对接焊实验。通过改变旋转速度、焊接速度、下压量等分析焊接工艺参数对焊缝成形质量的影响,分析接头各个微区的微观组织,探究焊核区第二相的分布特征,前进侧热机影响区析出第二相贫乏区的产生机理以及工艺参数对热机影响区形成析出第二相贫乏的影响。总结焊接接头微观组织,并结合维氏硬度、抗拉强度实验研究工艺参数对接头显微硬度、断裂特征的影响。 |
其他摘要 | The butt welding process of friction stir welding was used on 5 mm thick 7055 aluminum alloy. Effect of welding parameters on the quality of the welds were analyzed by the changing of the rotation rate、the welding speed and the pressure amount of shoulder. Then, microstructure of each micro-zone of the joints were analyzed, the distribution of the second phases in the nugget zone (NZ) and formation mechanisms and the influence of welding process of the particle depleted zone in thermo-mechanically affected zone (TMAZ) of advancing side were investigated. The influence of welding parameters on the micro-hardness and fracture characteristics of the joints combined with the Microstructures、the Vickers hardness and the tensile strength tests were investigated. |
页数 | 50 |
语种 | 中文 |
学号 | 122080503021 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/101827 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 霍仁杰. 铝合金7055搅拌摩擦对接焊接头微观组织与力学性能[D]. 兰州理工大学,2012. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[霍仁杰]的文章 |
百度学术 |
百度学术中相似的文章 |
[霍仁杰]的文章 |
必应学术 |
必应学术中相似的文章 |
[霍仁杰]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论