题名 | Ce对高铝青铜超音速等离子喷涂层组织及性能的影响 |
作者 | 施晓雨 |
学位类型 | 硕士 |
导师 | 路阳 |
答辩日期 | 2010 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料加工工程 |
关键词 | 高铝青铜合金 稀土元素Ce 超音速等离子喷涂 熔覆性 显微硬度 涂层与基体结合力 |
摘要 | 为了有效的改善高铝青铜合金涂层的组织性能。本课题采用添加稀土元素Ce对其进行性能改善处理。实验采用自主专利权的高铝青铜合金粉体,采用超音速等离子喷涂技术制备涂层。运用金相显微镜、X射线仪、EPMA电子探针、SEM扫描电子显微镜、显微硬度计以及万能试验机等设备分别对不同含铈量的涂层进行金相照片、物相组成、元素分布、界面形貌、硬度以及界面结合力强度等分析与检测。 |
其他摘要 | In order to effectively improve the performance of the high aluminum bronze alloy coating,this thesis used a method of adding rare earth element Ce to deal with it.The ultrafine powder used in this study which our research group had got its independent patent right was prepared through the method of gas atomization.Metallograph microscope,X-ray diffractometer,Electro-probe microanalyzer,Scanning electron microscope,Hardness tester and Universal testing machine were used to observe the microstructure,to detect the phases,to study the distribution of elements and to test hardness and interface bonding strength of the coatings. |
页数 | 57 |
语种 | 中文 |
学号 | 102080503082 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/100229 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 施晓雨. Ce对高铝青铜超音速等离子喷涂层组织及性能的影响[D]. 兰州理工大学,2010. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[施晓雨]的文章 |
百度学术 |
百度学术中相似的文章 |
[施晓雨]的文章 |
必应学术 |
必应学术中相似的文章 |
[施晓雨]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论