Fabrication and properties of a dense SiC NWs-toughened alpha-Si3N4 composite coating on porous Si3N4 ceramics | |
Shangguan, Duandan1; Wang, Binglei1; Wang, Chao1; Zhang, Fan1; Bai, Yu1; Wang, Zhanjie1; Lu, Xuefeng2 | |
2019-11-19 | |
发表期刊 | INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY |
ISSN | 1546-542X |
卷号 | 17期号:2页码:501-508 |
摘要 | A dense SiC nanowires-toughened alpha-Si3N4 coating was prepared using a two-step technique for protecting porous Si3N4 ceramic against mechanical damage, and effect of SiC nanowires content on microstructures and properties of the coating were investigated. XRD, SEM and TEM analysis results revealed that as-prepared coatings consisted of alpha-Si3N4, O'-Sialon, SiC nanowires and Y-Al-Si-O-N glass phase. Furthermore, Vickers hardness of the coated porous Si3N4 ceramics increased gradually with the increasing SiC nanowires content from 0 to 10 wt%, which is attributed to the gradual improvement in intrinsic elastic modulus (E), hardness (H) and H-3/E-2 of the coatings. But, when the SiC nanowires content was 15 wt%, the thickness of the coating became relatively thinner, so that its protective ability was weakened and Vickers hardness started to decrease accordingly. Meanwhile, the assistance of SiC nanowires enhanced fracture toughness of the coatings obviously because SiC nanowires in the coatings can produce various toughening mechanisms during mechanical damage. When the SiC nanowires content was 10 wt%, its fracture toughness reached the maximum value, which was 6.27 +/- 0.05 MPa center dot m(1/2). |
关键词 | porous Si3N4 properties SiC NWs-toughened alpha-Si3N4 coating toughening mechanism |
DOI | 10.1111/ijac.13419 |
收录类别 | SCI |
语种 | 英语 |
资助项目 | State Key Laboratory for Mechanical Behavior of Materials[20171905] ; Natural Science Foundation of Liaoning Province[20170520387] |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics |
WOS记录号 | WOS:000497075300001 |
出版者 | WILEY |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/76292 |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 |
通讯作者 | Wang, Chao |
作者单位 | 1.Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Liaoning, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Shangguan, Duandan,Wang, Binglei,Wang, Chao,et al. Fabrication and properties of a dense SiC NWs-toughened alpha-Si3N4 composite coating on porous Si3N4 ceramics[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2019,17(2):501-508. |
APA | Shangguan, Duandan.,Wang, Binglei.,Wang, Chao.,Zhang, Fan.,Bai, Yu.,...&Lu, Xuefeng.(2019).Fabrication and properties of a dense SiC NWs-toughened alpha-Si3N4 composite coating on porous Si3N4 ceramics.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,17(2),501-508. |
MLA | Shangguan, Duandan,et al."Fabrication and properties of a dense SiC NWs-toughened alpha-Si3N4 composite coating on porous Si3N4 ceramics".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 17.2(2019):501-508. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论