Effect of Cooling Rate on Microstructure and Properties of Heat-treated Fe(3)Al Intermetallics | |
Li, Yamin![]() ![]() | |
2011 | |
会议名称 | MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5 |
会议录名称 | MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5
![]() |
卷号 | 189-193 |
页码 | 3891-3894 |
出版地 | LAUBLSRUTISTR 24, CH-8717 STAFA-ZURICH, SWITZERLAND |
出版者 | TRANS TECH PUBLICATIONS LTD |
摘要 | The casting Fe(3)Al intermetallics were solidified in sodium silicate sand mould and permanent mould respectively to get different cooling rates. After heat treatment (1000 degrees C/15 h homogenizing annealing + furnace cooling followed by 600 degrees C/1 h tempering + oil quenching), the microstructure and properties of Fe(3)Al intermetallics were investigated. The results show that the heat-treated Fe(3)Al intermetallics at higher cooling rate has finer grained microstructure than lower cooling rate, and the lattice distortion increases due to the higher solid solubility of the elements Cr and B at higher cooling rate. The tensile strength and hardness of the Fe(3)Al intermetallics at higher cooling rate are slightly higher also. However, the impact power of intermetallics at higher cooling rate is 67.5% higher than that at lower cooling rate, and the impact fracture mode is also transformed from intercrystalline fracture at lower cooling rate to intercrystallin+transcrystalline mixed fracture at higher cooling rate. |
关键词 | Fe(3)Al Cooling Rate Heat Treatment Microstructure Property |
DOI | 10.4028/www.scientific.net/AMR.189-193.3891 |
收录类别 | CPCI |
语种 | 英语 |
WOS研究方向 | Engineering ; Materials Science |
WOS类目 | Engineering, Manufacturing ; Materials Science, Multidisciplinary |
WOS记录号 | WOS:000292279502059 |
引用统计 | |
文献类型 | 会议论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/37387 |
专题 | 国际教育学院 材料科学与工程学院 |
通讯作者 | Li, Yamin |
作者单位 | Lanzhou Univ Technol, Minist Educ, Key Lab Nonferrous Met Alloys & Proc, Lanzhou 730050, Gansu, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Li, Yamin,Liu, Hongjun,Hao, Yuan. Effect of Cooling Rate on Microstructure and Properties of Heat-treated Fe(3)Al Intermetallics[C]. LAUBLSRUTISTR 24, CH-8717 STAFA-ZURICH, SWITZERLAND:TRANS TECH PUBLICATIONS LTD,2011:3891-3894. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论