Facile synthesis of NZMC/Co3O4 composite electrode materials at low temperature and its application in electrochemical capacitor | |
Luo, Heming1; Sun, Yanxia1; Zhang, Fengbo2; Yang, Yanfei1; Zhao, Xia1 | |
2015-06 | |
发表期刊 | JOURNAL OF SOLID STATE ELECTROCHEMISTRY |
ISSN | 1432-8488 |
卷号 | 19期号:6页码:1717-1725 |
摘要 | A series of porous carbon/Co3O4 (NZMC-18(6)-700-3/Co3O4) composite materials with different cobalt contents were synthesized at low reaction temperature using a facile chemical precipitation method. The morphology and crystal structure of the materials were evaluated on field emission scanning electron microscope and X-ray diffraction, respectively. The results show that composite materials possess incompact lamellar structure with some irregular agglomerated Co3O4 particles adhering. The calcination temperature has a distinct influence on the morphology and electrochemical properties of porous carbon/Co3O4 composites. The electrochemical performances were measured by constant current charge/discharge tests, cyclic voltammetry, and electrochemical impedance spectroscopy tests. It is illustrated that the composite materials have outstanding charge storage ability and the specific capacitance can reach up to 462 F g(-1) when the calcination temperature and cobalt content are 250 A degrees C and 95 wt.%. With the increase of scan rate, the response current increases, and the anodic peaks and cathodic peaks shifted to higher potential and lower potential, respectively, which both illustrate that the material has excellent reversibility. The combination impedance of the electrode is only 0.674 Omega cm(2) at a calcination temperature of 250 A degrees C and is much less than those at other calcination temperatures which means that the electrode material has good conductivity. |
关键词 | Co3O4 Composite electrode materials Pseudocapacitance characteristics Electrochemical performance |
DOI | 10.1007/s10008-015-2803-1 |
收录类别 | SCI ; SCIE |
语种 | 英语 |
资助项目 | Funds for Creative Research Groups of China[51121062] ; Research Project for Education Department of Gansu province[1205ZTC032] ; Excellent Young Teachers Training Project in Lanzhou University of Technology[1005ZCX016] |
WOS研究方向 | Electrochemistry |
WOS类目 | Electrochemistry |
WOS记录号 | WOS:000354622700015 |
出版者 | SPRINGER |
EI入藏号 | 20151100621406 |
EI主题词 | Electrochemical electrodes |
EI分类号 | 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 641.1 Thermodynamics - 801 Chemistry - 802.3 Chemical Operations - 804 Chemical Products Generally - 933.1.1 Crystal Lattice - 951 Materials Science |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/34041 |
专题 | 石油化工学院 工会 |
通讯作者 | Zhao, Xia |
作者单位 | 1.Lanzhou Univ Technol, Sch Petrochem Engn, Lanzhou 730050, Gansu, Peoples R China; 2.Tianneng Battery Co Ltd, Changxing 313100, Zhejiang, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Luo, Heming,Sun, Yanxia,Zhang, Fengbo,et al. Facile synthesis of NZMC/Co3O4 composite electrode materials at low temperature and its application in electrochemical capacitor[J]. JOURNAL OF SOLID STATE ELECTROCHEMISTRY,2015,19(6):1717-1725. |
APA | Luo, Heming,Sun, Yanxia,Zhang, Fengbo,Yang, Yanfei,&Zhao, Xia.(2015).Facile synthesis of NZMC/Co3O4 composite electrode materials at low temperature and its application in electrochemical capacitor.JOURNAL OF SOLID STATE ELECTROCHEMISTRY,19(6),1717-1725. |
MLA | Luo, Heming,et al."Facile synthesis of NZMC/Co3O4 composite electrode materials at low temperature and its application in electrochemical capacitor".JOURNAL OF SOLID STATE ELECTROCHEMISTRY 19.6(2015):1717-1725. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论