Structure and electrochemical performance of highly porous carbons by single-step potassium humate carbonization for application in supercapacitors | |
Luo, HeMing; Yang, YanFei; Chen, YanZheng; Zhang, JianQiang; Zhao, Xia | |
2016-01 | |
发表期刊 | JOURNAL OF APPLIED ELECTROCHEMISTRY |
ISSN | 0021-891X |
卷号 | 46期号:1页码:113-121 |
摘要 | This paper presents the direct synthesis of highly porous carbons via the carbonization of potassium humate in inert atmosphere without any activation. Carbonization temperature is important for carbon structures and their electrochemical performance in electric double-layer capacitors. The CK800 material derived from potassium humate has a high-specific surface area of 890 m(2) g(-1) and an ideal average pore size of 2.56 nm. The CK800 material can also deliver a high-specific capacitance of 232 F g(-1) (26.1 A mu F cm(-2)) at a constant charge/discharge current of 0.5 A g(-1). This capacitance is maintained at a value of 114 F g(-1) (12.8 A mu F cm(-2)) at 30 A g(-1). This material also has good cycle stability with over 93.5 % capacitance retention after 5000 cycles when measured in a three-electrode system using 6 M KOH as electrolyte. In this study, the CK800 material is tested in a three-electrode system using 1 M NaHCO3 as electrolyte. Operational voltage in 1 M NaHCO3 aqueous solution could be extended up to 1.3 V. |
关键词 | Direct carbonization Supercapacitors High capacitance Mesoporous carbons Potassium humate |
DOI | 10.1007/s10800-015-0894-0 |
收录类别 | SCI ; SCIE |
语种 | 英语 |
资助项目 | National Natural Science Foundation of China (NSFC)[21364004][51462020] |
WOS研究方向 | Electrochemistry |
WOS类目 | Electrochemistry |
WOS记录号 | WOS:000367612100012 |
出版者 | SPRINGER |
EI入藏号 | 20154301437952 |
EI主题词 | Capacitance |
EI分类号 | 549.1 Alkali Metals - 701.1 Electricity: Basic Concepts and Phenomena - 802.2 Chemical Reactions - 804 Chemical Products Generally - 804.2 Inorganic Compounds - 951 Materials Science |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/33826 |
专题 | 石油化工学院 工会 |
通讯作者 | Luo, HeMing |
作者单位 | Lanzhou Univ Technol, Coll Petrochem Technol, Lanzhou 730050, Peoples R China |
第一作者单位 | 石油化工学院 |
通讯作者单位 | 石油化工学院 |
第一作者的第一单位 | 石油化工学院 |
推荐引用方式 GB/T 7714 | Luo, HeMing,Yang, YanFei,Chen, YanZheng,et al. Structure and electrochemical performance of highly porous carbons by single-step potassium humate carbonization for application in supercapacitors[J]. JOURNAL OF APPLIED ELECTROCHEMISTRY,2016,46(1):113-121. |
APA | Luo, HeMing,Yang, YanFei,Chen, YanZheng,Zhang, JianQiang,&Zhao, Xia.(2016).Structure and electrochemical performance of highly porous carbons by single-step potassium humate carbonization for application in supercapacitors.JOURNAL OF APPLIED ELECTROCHEMISTRY,46(1),113-121. |
MLA | Luo, HeMing,et al."Structure and electrochemical performance of highly porous carbons by single-step potassium humate carbonization for application in supercapacitors".JOURNAL OF APPLIED ELECTROCHEMISTRY 46.1(2016):113-121. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论