Enhancing Ductility of 1045 Nanoeutectic Steel Prepared by Aluminothermic Reaction through Annealing at 873K | |
Li, Zhengning; Wei, Fuan; La, Peiqing; Wang, Hongding; Wei, Yupeng | |
2017 | |
发表期刊 | ADVANCES IN MATERIALS SCIENCE AND ENGINEERING |
ISSN | 1687-8434 |
卷号 | 2017 |
摘要 | The 1045 steel with lamellar spacing of pearlite in nanometer was prepared by aluminothermic reaction casting and annealed at 873K (600 degrees C) with different time. Microstructures of steels were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM), and transmission electron microscope (TEM). Tensile properties of the steels were measured. The results showed that the lamellar spacing of the pearlite increased with the annealing time. It was found that the microstructure of steels consisted of nanocrystalline-ferritematrix and laminar pearlite phase. The average grain sizes of the ferrite were 26.9, 27.0, 26.1, and 34.9 nm for the cast steel and samples annealed for 2, 4, and 6 h, respectively. As the annealing time increased, the volume fraction of the pearlite almost remained constant, while the laminar spacing of pearlite increased from 146 to 300 nm. The tensile and yield strength varied slightly; the elongation obviously improved. After annealing for 4 h, the elongation increased to be 33%, which was the reported highest value for the steel up to now and about twice of the conventional 1045 steel. |
DOI | 10.1155/2017/5392073 |
收录类别 | SCI |
语种 | 英语 |
资助项目 | National Natural Science Foundation of China[51164022] ; Gansu Provincial Science and Technology Support Program[1304GKCA027] |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Multidisciplinary |
WOS记录号 | WOS:000394873600001 |
出版者 | HINDAWI LTD |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/33406 |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | La, Peiqing |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Li, Zhengning,Wei, Fuan,La, Peiqing,et al. Enhancing Ductility of 1045 Nanoeutectic Steel Prepared by Aluminothermic Reaction through Annealing at 873K[J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING,2017,2017. |
APA | Li, Zhengning,Wei, Fuan,La, Peiqing,Wang, Hongding,&Wei, Yupeng.(2017).Enhancing Ductility of 1045 Nanoeutectic Steel Prepared by Aluminothermic Reaction through Annealing at 873K.ADVANCES IN MATERIALS SCIENCE AND ENGINEERING,2017. |
MLA | Li, Zhengning,et al."Enhancing Ductility of 1045 Nanoeutectic Steel Prepared by Aluminothermic Reaction through Annealing at 873K".ADVANCES IN MATERIALS SCIENCE AND ENGINEERING 2017(2017). |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Li-2017-Enhancing Du(5886KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论