Metal Recovery from Spent LiMn2O4 Cathode Material Based on Sulfating Roasting with NaHSO4 center dot H2O and Water Leaching | |
Liu, Zhenning1; Chen, Huaijing2; Wang, Dahui1; Zhou, Xiaofang3; Hu, Pingping1 | |
2022-06 | |
发表期刊 | JOURNAL OF SUSTAINABLE METALLURGY |
ISSN | 2199-3823 |
卷号 | 8期号:2页码:684-699 |
摘要 | The reuse of waste materials helps to alleviate the pressure on sustainable economic development caused by the rapid consumption of natural resources. In this paper, a new process for the recovery of Li and Mn from spent LiMn2O4 cathode materials was studied. LiMn2O4 was mixed with NaHSO4 center dot H2O according to a certain mass ratio and roasted, and then the roasted products were leached with deionized water. The chemical changes during roasting were studied by thermogravimetric analysis, differential scanning calorimetry, X-ray diffraction, X-ray photoelectron spectroscopy, and scanning electron microscopy. After roasting, Li exists in the form of LiNaSO4, while the form of Mn is affected by the content of NNaHSO4 center dot H2O in the mixture. Within the corresponding temperature range, the chemical reaction between LiMn2O4 and NaHSO4 center dot H2O can proceed spontaneously. During the reaction, the following reactions will occur in the II and IV stages: NaHSO4 center dot H2O -> NaHSO4 + H2O(g), Na2S2O7 -> Na2SO4 + SO3 (g) and reaction of different metal oxides with SO3, and their average activation energies are 153.07 kJ/mol and 533.81 kJ/mol, respectively, and the restrictive link is three-dimensional diffusion. The roasted products were leached with deionized water, the extraction rate of Li and Mn elements increases with the decrease of mixing mass ratio, when the mass ratio of LiMn2O4 to NaHSO4 center dot H2O is 1:1.07, the roasting temperature is 873 K, the roasting time is 0.5 h, under the condition of water leaching temperature of 333 K, the extraction rates of Li and Mn were 96.6% and 9.7%, respectively. [GRAPHICS] . |
关键词 | Spent lithium-ion batteries LiMn2O4 Metal recovery Sulfating roasting Water leaching |
DOI | 10.1007/s40831-022-00519-7 |
收录类别 | SCIE ; EI |
语种 | 英语 |
WOS研究方向 | Science & Technology - Other Topics ; Metallurgy & Metallurgical Engineering |
WOS类目 | Green & Sustainable Science & Technology ; Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000773836900001 |
出版者 | SPRINGER |
EI入藏号 | 20221311873530 |
EI主题词 | X ray photoelectron spectroscopy |
EI分类号 | 445.1 Water Treatment Techniques ; 542.4 Lithium and Alloys ; 543.2 Manganese and Alloys ; 549.1 Alkali Metals ; 801 Chemistry ; 802.3 Chemical Operations ; 804.2 Inorganic Compounds ; 944.6 Temperature Measurements |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/158099 |
专题 | 理学院 材料科学与工程学院 |
通讯作者 | Wang, Dahui |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, Coll Sci, Lanzhou 730050, Peoples R China; 3.Gansu Prov Prod Qual Supervis & Inspect Res Inst, Lanzhou 730050, Peoples R China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Liu, Zhenning,Chen, Huaijing,Wang, Dahui,et al. Metal Recovery from Spent LiMn2O4 Cathode Material Based on Sulfating Roasting with NaHSO4 center dot H2O and Water Leaching[J]. JOURNAL OF SUSTAINABLE METALLURGY,2022,8(2):684-699. |
APA | Liu, Zhenning,Chen, Huaijing,Wang, Dahui,Zhou, Xiaofang,&Hu, Pingping.(2022).Metal Recovery from Spent LiMn2O4 Cathode Material Based on Sulfating Roasting with NaHSO4 center dot H2O and Water Leaching.JOURNAL OF SUSTAINABLE METALLURGY,8(2),684-699. |
MLA | Liu, Zhenning,et al."Metal Recovery from Spent LiMn2O4 Cathode Material Based on Sulfating Roasting with NaHSO4 center dot H2O and Water Leaching".JOURNAL OF SUSTAINABLE METALLURGY 8.2(2022):684-699. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论