Hot corrosion behavior of IN738LC alloy formed by selective laser melting | |
Hu, Yong1,2; Kang, Wenjiang1,3; Zhang, Huiying1,2; Chu, Cheng1,2; Wang, Lihua1,2; Hu, Yongqi1,2; Ding, Yutian1,2; Zhang, Dong4 | |
2022-04-15 | |
发表期刊 | Corrosion Science |
ISSN | 0010-938X |
卷号 | 198 |
摘要 | In this study, the hot corrosion of SLMed IN738LC and wrought GH738 alloy in mixed salt of 75%Na2SO4 + 25%NaCl at 900 is investigated. The results show that the hot corrosion of SLMed IN738LC is typically an acid-alkali fusion mechanism, the mass gains of SLMed IN738LC and wrought GH738 alloy are 0.61 mg/cm2 and 0.81 mg/cm2 after hot corrosion at 900 for 120 h, respectively. The double-layer oxide film of the SLMed sample presents better hot corrosion resistance, however, the corrosion occurs preferentially in cracks and the molten pool boundary. The corrosion performance of the SLMed sample shows obvious anisotropy. © 2022 Elsevier Ltd |
关键词 | Corrosion resistance Corrosion resistant alloys Corrosive effects Melting Oxide films Sodium chloride Sodium sulfate 75%na2SO4 + 25%nacl salt mixture Alkali fusion Corrosion behaviour Hot corrosion IN738LC alloy Mixed salts Polarization curves Salt mixtures Selective laser melting |
DOI | 10.1016/j.corsci.2022.110154 |
收录类别 | EI ; SCIE |
语种 | 英语 |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
WOS类目 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000781372500002 |
出版者 | Elsevier Ltd |
EI入藏号 | 20220611606712 |
EI主题词 | High temperature corrosion |
EI分类号 | 531 Metallurgy and Metallography ; 539.1 Metals Corrosion ; 802.3 Chemical Operations ; 804.2 Inorganic Compounds |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/157883 |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Hu, Yong |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Gansu, Peoples R China; 3.Chem & Chem Engn Guangdong Lab, Shantou 515031, Guangdong, Peoples R China; 4.Jinchuan Grp Co Ltd, State Key Lab Nickel & Cobalt Resources Comprehen, Jinchang 737100, Gansu, Peoples R China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 材料科学与工程学院 |
通讯作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 材料科学与工程学院 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Hu, Yong,Kang, Wenjiang,Zhang, Huiying,et al. Hot corrosion behavior of IN738LC alloy formed by selective laser melting[J]. Corrosion Science,2022,198. |
APA | Hu, Yong.,Kang, Wenjiang.,Zhang, Huiying.,Chu, Cheng.,Wang, Lihua.,...&Zhang, Dong.(2022).Hot corrosion behavior of IN738LC alloy formed by selective laser melting.Corrosion Science,198. |
MLA | Hu, Yong,et al."Hot corrosion behavior of IN738LC alloy formed by selective laser melting".Corrosion Science 198(2022). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论