Influences of thermal treatment temperature on microstructures and properties of glass-ceramics from gold tailings | |
Chen, Weiqian1,2; Li, Yuhong1; La, Peiqing2; Xue, Yangquan1; Li, Zengpeng1,2; Xu, Shipeng1,2; Sheng, Jie2 | |
2022 | |
发表期刊 | FERROELECTRICS |
ISSN | 0015-0193 |
卷号 | 579期号:1页码:23-32 |
摘要 | Use CaO-Al2O3-SiO2 glass-ceramics from gold tailings in Hanyin as main raw materials, which were prepared by a melting method. In this paper, the effects of nucleation temperature and crystallization temperature on microstructures and properties of the glass-ceramic specimens were investigated. The thermal property of the glass-ceramics was discussed by differential scanning calorimetry (DSC), and microstructure was characterized by X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Methods of a 4-point bending strength test, DIL-402C dilatometer and Archimedes method were used to determine the bending strength, thermal expanding coefficient and density of glass-ceramics. The experiment results indicated that the optimal properties of glass-ceramics were obtained by nucleation at 800 degrees C for 2 h, and then crystalling at 950 degrees C for 3 h. XRD analyses demonstrated that the main phase of gold tailings glass-ceramics was augite and diopside (CaMgSi2O6), and the minor phase was potassium iron silicate (KFeSi2O6). The bending strength, density and thermal expanding coefficient of the glass-ceramics were 128 MPa, 2.840 g/cm(3) and 7.85 x 10(-6)/degrees C, respectively. |
关键词 | Thermal treatment temperature gold tailings glass-ceramics melting method |
DOI | 10.1080/00150193.2021.1903264 |
收录类别 | EI ; SCOPUS ; SCIE |
语种 | 英语 |
WOS研究方向 | Materials Science ; Physics |
WOS类目 | Materials Science, Multidisciplinary ; Physics, Condensed Matter |
WOS记录号 | WOS:000684976200002 |
出版者 | TAYLOR & FRANCIS LTD |
EI入藏号 | 20213310785843 |
EI分类号 | 531.2 Metallography - 535.2 Metal Forming - 547.1 Precious Metals - 549.3 Nonferrous Metals and Alloys excluding Alkali and Alkaline Earth Metals - 802.3 Chemical Operations - 804.2 Inorganic Compounds - 933.1.2 Crystal Growth - 944.6 Temperature Measurements - 951 Materials Science |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/148710 |
专题 | 学科建设与学位办公室 材料科学与工程学院 |
通讯作者 | Li, Yuhong |
作者单位 | 1.Jiuquan Vocat & Tech Coll, Key Lab Solar Power Syst Engn, Jiuquan, Gansu, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou, Peoples R China |
第一作者单位 | 材料科学与工程学院 |
推荐引用方式 GB/T 7714 | Chen, Weiqian,Li, Yuhong,La, Peiqing,et al. Influences of thermal treatment temperature on microstructures and properties of glass-ceramics from gold tailings[J]. FERROELECTRICS,2022,579(1):23-32. |
APA | Chen, Weiqian.,Li, Yuhong.,La, Peiqing.,Xue, Yangquan.,Li, Zengpeng.,...&Sheng, Jie.(2022).Influences of thermal treatment temperature on microstructures and properties of glass-ceramics from gold tailings.FERROELECTRICS,579(1),23-32. |
MLA | Chen, Weiqian,et al."Influences of thermal treatment temperature on microstructures and properties of glass-ceramics from gold tailings".FERROELECTRICS 579.1(2022):23-32. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论