Microstructure and Properties of Composite Modified Layer of Austenitic Stainless Steel Obtained by Nitriding & Physical Vapor Deposition | |
Chen, Zhilin1; Cao, Chi1,2; Yang, Ruicheng1,2; Mu, Xinbin1; Chen, Bibi1; Hu, Qiuchen2 | |
2021-03-25 | |
发表期刊 | Cailiao Daobao/Materials Reports |
ISSN | 1005-023X |
卷号 | 35期号:6页码:6161-6166 |
摘要 | Austenitic stainless steel 316L was ion nitrided by glow plasma penetration and diffusion technique at different temperatures, subsequently, CrN coating was deposited on top of the nitrided layer by physical vapor deposition technology. The adhesion strength, hardness, tribological property and corrosion resistance of the duplex coating were tested. The microstructure and phase constituents were also examined. It has been found that, with the increase of temperature, the microconstituent of the duplex coating gained by plasma nitriding at different temperatures and PVD transfers from S-phase (inner layer)+CrN coating (outer layer) to hard phase precipitated layer of different degree (inner layer)+CrN coa-ting (outer layer). The adhesion strength of different kinds of nitrided layer with CrN coating was good. After PVD treatment, the surface hardness, abrasion resistance and corrosion resistance of nitrided layer was improved to some extent whether it was S-phase or hard phase precipitated layer. With the increase of nitriding temperature, the corrosion resistance deteriorated, the hardness and abrasion resistance were elevated. © 2021, Materials Review Magazine. All right reserved. |
关键词 | Abrasion Adhesion Aluminum nitride Bond strength (materials) Corrosion resistance Corrosion resistant coatings Diffusion coatings Erosion Hardness Microstructure Nitriding Physical vapor deposition Plasma applications Steel corrosion Wear resistance Austenitic stainless Duplex coatings Microstructure and properties Nitriding temperatures Phase constituent Plasma nitriding Surface hardness Tribological properties |
DOI | 10.11896/cldb.19120214 |
收录类别 | EI |
语种 | 中文 |
出版者 | Cailiao Daobaoshe/ Materials Review |
EI入藏号 | 20211710243101 |
EI主题词 | Austenitic stainless steel |
EI分类号 | 537.1 Heat Treatment Processes ; 539.1 Metals Corrosion ; 545.3 Steel ; 804.1 Organic Compounds ; 813.2 Coating Materials ; 931.2 Physical Properties of Gases, Liquids and Solids ; 932.3 Plasma Physics ; 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/148445 |
专题 | 温州泵阀工程研究院 |
作者单位 | 1.Wenzhou Pump and Valve Engineering Research Institute of Lanzhou University of Technology, Wenzhou; 325105, China; 2.Institute of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China |
第一作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Chen, Zhilin,Cao, Chi,Yang, Ruicheng,et al. Microstructure and Properties of Composite Modified Layer of Austenitic Stainless Steel Obtained by Nitriding & Physical Vapor Deposition[J]. Cailiao Daobao/Materials Reports,2021,35(6):6161-6166. |
APA | Chen, Zhilin,Cao, Chi,Yang, Ruicheng,Mu, Xinbin,Chen, Bibi,&Hu, Qiuchen.(2021).Microstructure and Properties of Composite Modified Layer of Austenitic Stainless Steel Obtained by Nitriding & Physical Vapor Deposition.Cailiao Daobao/Materials Reports,35(6),6161-6166. |
MLA | Chen, Zhilin,et al."Microstructure and Properties of Composite Modified Layer of Austenitic Stainless Steel Obtained by Nitriding & Physical Vapor Deposition".Cailiao Daobao/Materials Reports 35.6(2021):6161-6166. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论