Effect of corrosion pits on fatigue life and crack initiation | |
Zhang, Xin-Yan1; Li, Shu-Xin1; Liang, Rui1![]() | |
2013 | |
会议名称 | 13th International Conference on Fracture 2013, ICF 2013 |
会议录名称 | 13th International Conference on Fracture 2013, ICF 2013
![]() |
卷号 | 2 |
页码 | 1667-1675 |
会议日期 | June 16, 2013 - June 21, 2013 |
会议地点 | Beijing, China |
出版者 | Chinese Society of Theoretical and Applied Mechanics |
摘要 | Corrosion fatigue is identified as one of the main failure mechanism for structures working in corrosive environment. The existing study on pit corrosion showed that cracks do not necessarily initiate from the bottom of the pit. Where the crack initiate from pit depends on the pit shape (aspect ratio), loading and the corrosive environment. In this study, firstly, the corrosion pit development in size and shape and its effect on fatigue life were reviewed. Fatigue tests were conducted on pre-pitted and smooth samples to further investigate the pit effect. Then various aspect ratios of pits were modeled to calculate the SCF in a round bar under tension and bending loadings. In addition, the SCF of a wide range of aspect ratios of pits were calculated, by which it is expected to offer the engineering practice and researchers convenience to find SCF value. |
关键词 | Aspect ratio Corrosion fatigue Failure (mechanical) Fatigue testing Pitting Stress concentration Bending loading Corrosion pits Corrosive environment Engineering practices Failure mechanism Pit corrosion Size and shape Stress concentration factors |
收录类别 | EI |
语种 | 英语 |
EI入藏号 | 20141717628436 |
EI主题词 | Cracks |
来源库 | Compendex |
分类代码 | 539.1 Metals Corrosion |
文献类型 | 会议论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/117860 |
专题 | 石油化工学院 |
作者单位 | 1.School of PetroChemical Engineering, Lanzhou University of Technology, Lanzhou 730050, China; 2.Corrosion and Protection Centre, School of Materials, University of Manchester, Manchester M13 9PL, United Kingdom |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Zhang, Xin-Yan,Li, Shu-Xin,Liang, Rui,et al. Effect of corrosion pits on fatigue life and crack initiation[C]:Chinese Society of Theoretical and Applied Mechanics,2013:1667-1675. |
条目包含的文件 | 条目无相关文件。 |