Cleavage initiation mechanism in notched specimens of steel with carbides and inclusions | |
Wang, G.Z.; Chen, J.H. | |
2005 | |
会议名称 | 11th International Conference on Fracture 2005, ICF11 |
会议录名称 | 11th International Conference on Fracture 2005, ICF11 |
卷号 | 6 |
页码 | 4217-4222 |
会议日期 | March 20, 2005 - March 25, 2005 |
会议地点 | Turin, Italy |
出版者 | International Congress on Fracture |
摘要 | Cleavage initiation mechanism in notched specimens of steel with carbides and inclusions is investigated at -196 °C and -130 °C. The mechanical tests, microscopic observations and measurements, and FEM calculations are carried out. Two types of cleavage initiation sites are found. One is related to approximately spherical inclusions ahead of notch root (IC initiation), the other is related to spherical inclusions situated ahead of elongated larger string inclusions (SIC initiation). In both IC and SIC initiation mechanism, the crack nucleation is induced by inclusions and the final fracture is controlled by propagation of a ferrite grain-sized crack into matrix grain. In the case of SIC initiation, a plate-like defect caused by the early debonding of the elongated larger string inclusions promotes the cleavage fracture, and the cleavage initiates in front of the plate-like defect. Temperature has pronounced effect on the type of the cleavage initiation site. At -196 °C the fractures are mainly the IC initiation mechanism, and at -130 °C all the fractures are the SIC initiation mechanism. The reason for this has been analyzed. The notch toughness of the steels tested is mainly determined by the cleavage initiation occurring in the weak constituents composed of inclusions and matrix grains, and is independent on the sizes and numbers of carbide particles. |
关键词 | Carbides Fracture Integrated circuits Carbide particles Cleavage fracture Crack nucleation Initiation mechanism Initiation sites Microscopic observations Notched specimens Spherical inclusion |
收录类别 | EI |
语种 | 英语 |
EI入藏号 | 20124815728200 |
EI主题词 | Cracks |
来源库 | Compendex |
分类代码 | 714.2 Semiconductor Devices and Integrated Circuits - 804.2 Inorganic Compounds - 951 Materials Science |
文献类型 | 会议论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/117156 |
专题 | 材料科学与工程学院_特聘教授组 |
作者单位 | State Key Laboratory of New Nonferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Wang, G.Z.,Chen, J.H.. Cleavage initiation mechanism in notched specimens of steel with carbides and inclusions[C]:International Congress on Fracture,2005:4217-4222. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[Wang, G.Z.]的文章 |
[Chen, J.H.]的文章 |
百度学术 |
百度学术中相似的文章 |
[Wang, G.Z.]的文章 |
[Chen, J.H.]的文章 |
必应学术 |
必应学术中相似的文章 |
[Wang, G.Z.]的文章 |
[Chen, J.H.]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论