Microstructure and bending deformation about the surface composite materials on copper substrate | |
Yang, Guirong1,2; Song, Wenming1,2; Hao, Yuan1,2; Ma, Ying1,2 | |
2006-12-01 | |
发表期刊 | Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research |
ISSN | 10053093 |
卷号 | 20期号:6页码:631-636 |
摘要 | The microstructure of surface Ni-based infiltrated layer on copper substrate and the bending behavior were investigated. It was found the Ni-based infiltrated layer consist of surface sintering layer (SSL), metallurgical fusion layer {MFL} and diffusion solid solution layer (DSSL). The SSL is composed of CrB, Cr3Ni2 and Ni-based solid solution, and the MFL is composed of CrB and Ni-based solid solution, while the Ni-based solid solution and Cu-based solid solution of high content are observed in DSSL. The Ni-based infiltration layer is located on the top or at the bottom of the sample in the bending experiment, respectively. There are yielding elongation point and peak value at the stress-strain curve comparing with that of the substrate, respectively. The bending strength is improved separately by 76% and 32.9% at the same strain comparing with the substrate. The SSL peeled off or cracked when the infiltrated layer failed. |
关键词 | Bending strength Casting Infiltration Microstructure Sintering Solid solutions Diffusion solid solution layer (DSSL) Metallurgical fusion layer (MFL) Surface nickel based infiltrated layer Surface sintering layer (SSL) Vacuum infiltration casting |
收录类别 | EI |
语种 | 中文 |
出版者 | Chinese Journal of Materials Research, 72 Wenhua Road, Shenyang, 110015, China |
EI入藏号 | 20071010470986 |
EI主题词 | Composite materials |
EI分类号 | 415 Metals, Plastics, Wood and Other Structural Materials - 534.2 Foundry Practice - 802.3 Chemical Operations |
来源库 | Compendex |
分类代码 | 415 Metals, Plastics, Wood and Other Structural Materials - 534.2 Foundry Practice - 802.3 Chemical Operations |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/111936 |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China; 2.Key Laboratory of Non-ferrous Metal Alloys, Lanzhou University of Technology, Lanzhou 730050, China |
第一作者单位 | 省部共建有色金属先进加工与再利用国家重点实验室; 兰州理工大学 |
第一作者的第一单位 | 省部共建有色金属先进加工与再利用国家重点实验室 |
推荐引用方式 GB/T 7714 | Yang, Guirong,Song, Wenming,Hao, Yuan,et al. Microstructure and bending deformation about the surface composite materials on copper substrate[J]. Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,2006,20(6):631-636. |
APA | Yang, Guirong,Song, Wenming,Hao, Yuan,&Ma, Ying.(2006).Microstructure and bending deformation about the surface composite materials on copper substrate.Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,20(6),631-636. |
MLA | Yang, Guirong,et al."Microstructure and bending deformation about the surface composite materials on copper substrate".Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research 20.6(2006):631-636. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论