题名 | 低合金钢在不同低温下解理断裂机理的研究 |
作者 | 李广![]() |
学位类型 | 硕士 |
导师 | 陈剑虹 ; 曹睿 |
答辩日期 | 2006 |
学位授予单位 | 兰州理工大学 |
学位名称 | 工学硕士 |
学位专业 | 材料学 |
关键词 | 韧脆转变 塑性裂纹扩展 断裂韧性 解理起裂源 有限元 |
摘要 | 本文对三种微观组织(细晶细碳化物、细晶粗碳化物、粗晶粗碳化物)的16MnR钢三点弯曲预裂纹试样的解理断裂进行了详细地研究。 |
其他摘要 | Based on observations of fracture surfaces and measurements of local critical parameters, analysis and comparison of nature of cleavage triggering sites at various temperature for different microstructure steel, analysis of relationship between ductile crack propagation length and fracture toughness, sophisticated FEM calculations of distributions of stress, strain and triaxiality and simulations of short cracks initiated and extended at precrack tips, the cleavage fracture are studied for three point bending(3PB) precracked specimens with three various microstructure, the followed main conclusions are obtained. |
页数 | 103 |
语种 | 中文 |
学号 | 062080502040 |
文献类型 | 学位论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/97421 |
专题 | 兰州理工大学 |
作者单位 | 兰州理工大学 |
第一作者单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | 李广. 低合金钢在不同低温下解理断裂机理的研究[D]. 兰州理工大学,2006. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
查看访问统计 |
谷歌学术 |
谷歌学术中相似的文章 |
[李广]的文章 |
百度学术 |
百度学术中相似的文章 |
[李广]的文章 |
必应学术 |
必应学术中相似的文章 |
[李广]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论