Review of the damage mechanism in wind turbine gearbox bearings under rolling contact fatigue | |
Su, Yun-Shuai1; Yu, Shu-Rong1; Li, Shu-Xin1,2; He, Yan-Ni1 | |
2019-12 | |
发表期刊 | FRONTIERS OF MECHANICAL ENGINEERING |
ISSN | 2095-0233 |
卷号 | 14期号:4页码:434-441 |
摘要 | Wind turbine gearbox bearings fail with the service life is much shorter than the designed life. Gearbox bearings are subjected to rolling contact fatigue (RCF) and they are observed to fail due to axial cracking, surface flaking, and the formation of white etching areas (WEAs). The current study reviewed these three typical failure modes. The underlying dominant mechanisms were discussed with emphasis on the formation mechanism of WEAs. Although numerous studies have been carried out, the formation of WEAs remains unclear. The prevailing mechanism of the rubbing of crack faces that generates WEAs was questioned by the authors. WEAs were compared with adiabatic shear bands (ASBs) generated in the high strain rate deformation in terms of microstructural compositions, grain refinement, and formation mechanism. Results indicate that a number of similarities exist between them. However, substantial evidence is required to verify whether or not WEAs and ASBs are the same matters. |
关键词 | rolling contact fatigue (RCF) white etching area (WEA) white etching crack (WEC) adiabatic shear band (ASB) |
DOI | 10.1007/s11465-018-0474-1 |
收录类别 | SCI ; SCIE |
语种 | 英语 |
资助项目 | National Natural Science Foundation of China[51275225] |
WOS研究方向 | Engineering |
WOS类目 | Engineering, Mechanical |
WOS记录号 | WOS:000509917100006 |
出版者 | HIGHER EDUCATION PRESS |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/76463 |
专题 | 兰州理工大学 |
通讯作者 | Yu, Shu-Rong; Li, Shu-Xin |
作者单位 | 1.Lanzhou Univ Technol, Sch PetroChem Engn, Lanzhou 730050, Peoples R China; 2.Ningbo Univ, Sch Mech Engn & Mech, Ningbo 315211, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Su, Yun-Shuai,Yu, Shu-Rong,Li, Shu-Xin,et al. Review of the damage mechanism in wind turbine gearbox bearings under rolling contact fatigue[J]. FRONTIERS OF MECHANICAL ENGINEERING,2019,14(4):434-441. |
APA | Su, Yun-Shuai,Yu, Shu-Rong,Li, Shu-Xin,&He, Yan-Ni.(2019).Review of the damage mechanism in wind turbine gearbox bearings under rolling contact fatigue.FRONTIERS OF MECHANICAL ENGINEERING,14(4),434-441. |
MLA | Su, Yun-Shuai,et al."Review of the damage mechanism in wind turbine gearbox bearings under rolling contact fatigue".FRONTIERS OF MECHANICAL ENGINEERING 14.4(2019):434-441. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论