Effect of Alloy Element Al on the Corrosion Behavior of Ni-10wt%Fe Based Alloy in Molten NaCl
Wang Junwei1; Jia Hongguang1; Wang Zhiping2; Zhu Tong3; Lei Fujun1; Xu Jun3
2017
Source Publication稀有金属材料与工程
ISSN1002-185X
Volume46Issue:1Pages:57-62
AbstractNaCl and its mixed salt have many advantages as a medium of solar energy phase change thermal storage at moderate and high temperature. But molten chloride has sharp corrosive action on metal thermal storage vessel. The corrosion behavior of three kinds of Ni-10 wt% Fe based alloy (1#, 2# and 3#) in 850 °C molten NaCl was studied. The content of Al in 1#, 2# and 3# sample was 0.0 wt%, 5.0 wt% and 10.0 wt%, respectively. The components of NaCl after corroding and corrosion products on samples surface were analyzed. Elements change trend and corrosion characteristics on cross section of the three samples were contrasted. Corrosion mechanisms were discussed finally. Results show that the kinetics curves of the three kinds of sample obey a liner rule. The average mass loss rate declines when Al is added in the sample. The rate of 2# and 3# is only 12% and 20% of that of 1#, respectively. There are two reasons for the value reduction: firstly, Al will be oxidized prior to oxidization of Fe or Ni, and the atomic mass of Al is small; secondly, Al_2O_3 is very stable at high temperature as corrosion products. However, when the content of Al is very high (for example 10 wt% in here) in Ni-10 wt% Fe based alloy, Al oxidized on sample surface provides a convenient condition for Al atom transmission from sample inside to surface. Al_2O_3 film becomes thick and exfoliates easily. The exfoliation increases the average mass loss rate in turn.
Keywordcorrosion molten salt NaCl Al NaCl Al
Indexed ByCSCD
Language英语
WOS Research AreaMetallurgy & Metallurgical Engineering
WOS SubjectMETALLURGY METALLURGICAL ENGINEERING
CSCD IDCSCD:5902147
Document Type期刊论文
Identifierhttp://ir.lut.edu.cn/handle/2XXMBERH/72291
Collection兰州理工大学
Affiliation1.Qinghai University, National Engineering Research Center of High Performance Light Metal Alloys and Forming, Xining, Qinghai 810016, China
2.Lanzhou University of Technology, Lanzhou, Gansu 730050, China
3.Qinghai University, Xining, Qinghai 810016, China
Recommended Citation
GB/T 7714
Wang Junwei,Jia Hongguang,Wang Zhiping,et al. Effect of Alloy Element Al on the Corrosion Behavior of Ni-10wt%Fe Based Alloy in Molten NaCl[J]. 稀有金属材料与工程,2017,46(1):57-62.
APA Wang Junwei,Jia Hongguang,Wang Zhiping,Zhu Tong,Lei Fujun,&Xu Jun.(2017).Effect of Alloy Element Al on the Corrosion Behavior of Ni-10wt%Fe Based Alloy in Molten NaCl.稀有金属材料与工程,46(1),57-62.
MLA Wang Junwei,et al."Effect of Alloy Element Al on the Corrosion Behavior of Ni-10wt%Fe Based Alloy in Molten NaCl".稀有金属材料与工程 46.1(2017):57-62.
Files in This Item:
There are no files associated with this item.
Related Services
Usage statistics
Google Scholar
Similar articles in Google Scholar
[Wang Junwei]'s Articles
[Jia Hongguang]'s Articles
[Wang Zhiping]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang Junwei]'s Articles
[Jia Hongguang]'s Articles
[Wang Zhiping]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang Junwei]'s Articles
[Jia Hongguang]'s Articles
[Wang Zhiping]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.