Toughening Effect of ZrB_2 in Al_2O_3-ZrB_2 Nanocomposite Ceramics
Wang Xiaomin1; La Peiqing1; Wang Bingjun2; Yang Guolai1
2016
Source Publication稀有金属材料与工程
ISSN1002-185X
Volume45Issue:7Pages:1714-1718
AbstractThe Al_2O_3-ZrB_2 nanocomposite ceramics were prepared and the mechanical properties of the process parameters effect were studied. The results show that for various applied sintering temperatures of Al_2O_3 ceramics, a maximum Vickers hardness of 18 970 MPa and high reliability are attained at 1500 °C and at atmosphere sintering. The fracture toughness is (5.20.3) MPa·m~(1/2). In addition, the sample is not well densified at the sintering temperature. Scanning electron microscopy (SEM) shows that fine ZrB_2 particles disperse and are pinned at grain boundaries to inhibit grain boundary movement effectively. While larger ZrB_2 particles distribute between A1_2O_3 particles uniformly and occupy Al_2O_3 particles growing space to hinder the matrix grains, which greatly promote the densification of the ceramic and improve the microstructure. 20% ZrB_2/Al_2O_3 composite ceramics exhibit a relative density above 98% at (450 °C, Vickers hardness of 18 070 MPa, and fracture toughness of (6.70.2) MPa·m~(1/2) Fracture morphology indicates that trans-granular fracture occurs in the nanocomposite ceramic with high toughness.
Keywordatmospheric sintering nano alumina ceramic nanocomposite ceramics toughening
Indexed ByCSCD
Language英语
WOS Research AreaEngineering
WOS SubjectENGINEERING CHEMICAL
CSCD IDCSCD:5758148
Document Type期刊论文
Identifierhttp://ir.lut.edu.cn/handle/2XXMBERH/71743
Collection材料科学与工程学院
兰石研究院(新区研究院)
Affiliation1.Lanzhou University of Technology, State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou, Gansu 730050, China
2.Qinghai University, Xining, Qinghai 810016, China
First Author AffilicationLanzhou University of Technology
First Signature AffilicationLanzhou University of Technology
Recommended Citation
GB/T 7714
Wang Xiaomin,La Peiqing,Wang Bingjun,et al. Toughening Effect of ZrB_2 in Al_2O_3-ZrB_2 Nanocomposite Ceramics[J]. 稀有金属材料与工程,2016,45(7):1714-1718.
APA Wang Xiaomin,La Peiqing,Wang Bingjun,&Yang Guolai.(2016).Toughening Effect of ZrB_2 in Al_2O_3-ZrB_2 Nanocomposite Ceramics.稀有金属材料与工程,45(7),1714-1718.
MLA Wang Xiaomin,et al."Toughening Effect of ZrB_2 in Al_2O_3-ZrB_2 Nanocomposite Ceramics".稀有金属材料与工程 45.7(2016):1714-1718.
Files in This Item:
There are no files associated with this item.
Related Services
Usage statistics
Google Scholar
Similar articles in Google Scholar
[Wang Xiaomin]'s Articles
[La Peiqing]'s Articles
[Wang Bingjun]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang Xiaomin]'s Articles
[La Peiqing]'s Articles
[Wang Bingjun]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang Xiaomin]'s Articles
[La Peiqing]'s Articles
[Wang Bingjun]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.