Investigation of fracture mechanism of 6063 aluminum alloy under different stress states | |
Zhu, Hao2; Zhu, Liang1,2; Chen, Jian-Hong1,2; Lv, Xian-Feng2 | |
2007-08 | |
发表期刊 | INTERNATIONAL JOURNAL OF FRACTURE |
ISSN | 0376-9429 |
卷号 | 146期号:3页码:159-172 |
摘要 | Fracture mechanisms in a 6063 aluminum alloy were investigated and analyzed carefully by in-situ tensile tests in SEM with a vacuum chamber. Specimens used were designed to produce different stress states. Studies indicated that with stress triaxiality (sigma(m)/sigma(e)) decreasing, the fracture modes changed from normal fracture to shear fracture and the fracture surfaces changed from the dimples and intragranular dominated fracture mode to the shear dominated fracture mode. The grain boundaries of the 6063 alurninum alloy were the weakest positions. In the case of high stress triaxiality, the grain boundary cracks were produced by normal stress or by the incompatibility of deformation between neighboring grains, and the normal stress dominated the crack propagation. In the case of low stress triaxiality, the boundary cracks were produced by the relative slipping of grains against neighboring grains, and the shear stress dominated the crack propagation. The final fracture of the specimens occurred by connections of cracks through transgranular cracking of the ligaments among these cracks. |
关键词 | 6063 aluminum alloy in-situ tensile test fracture process fracture mechanism |
DOI | 10.1007/s10704-007-9158-2 |
收录类别 | SCI ; SCIE |
语种 | 英语 |
WOS研究方向 | Materials Science ; Mechanics |
WOS类目 | Materials Science, Multidisciplinary ; Mechanics |
WOS记录号 | WOS:000251976500004 |
出版者 | SPRINGER |
EI入藏号 | 20075010973328 |
EI主题词 | Aluminum alloys |
EI分类号 | 422.2 Strength of Building Materials : Test Methods - 541.2 Aluminum Alloys - 951 Materials Science |
引用统计 | 无
|
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/35590 |
专题 | 材料科学与工程学院_特聘教授组 材料科学与工程学院 |
通讯作者 | Chen, Jian-Hong |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Nonferrous Met Mat, Lanzhou 730050, Peoples R China 2.Lanzhou Univ Technol, Coll Mat Sci & Engn, Lanzhou 730050, Peoples R China |
第一作者单位 | 材料科学与工程学院 |
通讯作者单位 | 兰州理工大学; 材料科学与工程学院 |
第一作者的第一单位 | 材料科学与工程学院 |
推荐引用方式 GB/T 7714 | Zhu, Hao,Zhu, Liang,Chen, Jian-Hong,et al. Investigation of fracture mechanism of 6063 aluminum alloy under different stress states[J]. INTERNATIONAL JOURNAL OF FRACTURE,2007,146(3):159-172. |
APA | Zhu, Hao,Zhu, Liang,Chen, Jian-Hong,&Lv, Xian-Feng.(2007).Investigation of fracture mechanism of 6063 aluminum alloy under different stress states.INTERNATIONAL JOURNAL OF FRACTURE,146(3),159-172. |
MLA | Zhu, Hao,et al."Investigation of fracture mechanism of 6063 aluminum alloy under different stress states".INTERNATIONAL JOURNAL OF FRACTURE 146.3(2007):159-172. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论