Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy | |
Liu Dexue1,2; Cheng Xiaowei1,2; Zhang Xiao1,2; Ding Yutian1,2 | |
2016-12 | |
发表期刊 | JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION |
ISSN | 1000-2413 |
卷号 | 31期号:6页码:1368-1376 |
摘要 | The effects of the heating process and hot extrusion on the microstructure and properties of inconel 625 alloy were studied. The experimental results showed that the properties of Inconel 625 alloy could be improved through the heating process and hot extrusion concomitant with a reduced corrosion rate. The M23C6 carbide, generated in the heating process, was retained and distributed at the grain boundary during the process of hot extrusion, which had an important influence on both elongation and corrosion resistance. The improvement of the comprehensive properties of the material, as measured by a tensile test at room temperature, was correlated with the dissolution of segregation Nb. A typical ductile fracture changed to a cleavage fracture where secondary cracks could be clearly seen. With the increase of the extrusion ratio, the real extrusion temperature was higher, which led to more dissolution of the M23C6 carbide, decreased the number of secondary cracks, enhanced the effect of solid solution strengthening, and reduced the intergranular corrosion rate. Under the condition of a high extrusion ratio and a high extrusion speed, the less extrusion time made it possible to obtain organization with a smaller average grain size. Moreover, in this case, the M23C6 carbide and segregated Nb did not have enough time to diffuse. Thus all samples exhibited medium strengths and corrosion rates after extrusion. |
关键词 | Inconel 625 alloy hot extrusion mechanical property microstructure evolution |
DOI | 10.1007/s11595-016-1540-3 |
收录类别 | SCI |
语种 | 英语 |
资助项目 | National Natural Science Foundation of China[51664041][51365029] ; Gansu Science and Technology Support Program-industrial Category[1604GKCA038] ; Program for Major Projects of Science and Technology in Gansu Province[145RTSA004] |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Multidisciplinary |
WOS记录号 | WOS:000393051300032 |
出版者 | WUHAN UNIV TECHNOLOGY |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/33519 |
专题 | 材料科学与工程学院 外国语学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China; 2.State Key Lab Adv Proc & Recyling Nonferrous Met, Lanzhou 730050, Peoples R China |
第一作者单位 | 材料科学与工程学院 |
第一作者的第一单位 | 材料科学与工程学院 |
推荐引用方式 GB/T 7714 | Liu Dexue,Cheng Xiaowei,Zhang Xiao,et al. Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy[J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,2016,31(6):1368-1376. |
APA | Liu Dexue,Cheng Xiaowei,Zhang Xiao,&Ding Yutian.(2016).Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy.JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,31(6),1368-1376. |
MLA | Liu Dexue,et al."Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy".JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION 31.6(2016):1368-1376. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Liu-2016-Effects of (2594KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论