Mesoscopic transformation at initial corrosion stage of 20# steel in aqueous solution under gas-liquid two-phase stratified flow condition | |
Yang, Guirong1; Pan, Zhaoxia1; Zhang, Zhenghai1; Song, Wenming2; Ma, Ying1; Hao, Yuan1 | |
2021-05-25 | |
发表期刊 | ANTI-CORROSION METHODS AND MATERIALS |
ISSN | 0003-5599 |
卷号 | 68期号:2页码:53-63 |
摘要 | Purpose This study aims to investigate the initial corrosion behavior in aqueous solution of 20# seamless steel under (CO2/aqueous solution) gas-liquid two-phase stratified flow conditions. Design/methodology/approach The initial corrosion behavior was studied through the weight loss methods, scanning electron microscopy with energy-dispersive x-ray spectroscopy and x-ray diffraction. Findings The corrosion rate of 20# steel obviously increases with the increasing gas pressure at different corrosion time when the CO2 pressure is less than 0.11 MPa, and the increase of corrosion rate tends to be steady when the pressure exceeds 0.11 MPa. With the increase of CO2 pressure, the corrosion products changed from flocculent to acicular, granular and scaly. A four-stage model for the growth of the corrosion product layer was proposed, namely, the diffusion reaction stage, the local film formation stage, the complete film formation stage and the densification stage of the product film. Originality/value A four-stage model for the growth of the corrosion product layer on the pipe wall surface under this condition was proposed, namely, the diffusion reaction stage, the local film formation stage, the complete film formation stage and the densification stage of the product film. The growing process and densification mechanism of corrosion products layer were discussed. |
关键词 | CO2 corrosion Stratified flow Corrosion product layer growth model Densification process |
DOI | 10.1108/ACMM-02-2020-2257 |
收录类别 | SCIE ; SCOPUS ; EI |
语种 | 英语 |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
WOS类目 | Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000634607100001 |
出版者 | EMERALD GROUP PUBLISHING LTD |
来源库 | WOS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | https://ir.lut.edu.cn/handle/2XXMBERH/148290 |
专题 | 材料科学与工程学院 |
通讯作者 | Yang, Guirong |
作者单位 | 1.Lanzhou Univ Technol, Lanzhou, Peoples R China; 2.Lanpec Technol Ltd, Lanzhou, Peoples R China |
第一作者单位 | 兰州理工大学 |
通讯作者单位 | 兰州理工大学 |
第一作者的第一单位 | 兰州理工大学 |
推荐引用方式 GB/T 7714 | Yang, Guirong,Pan, Zhaoxia,Zhang, Zhenghai,et al. Mesoscopic transformation at initial corrosion stage of 20# steel in aqueous solution under gas-liquid two-phase stratified flow condition[J]. ANTI-CORROSION METHODS AND MATERIALS,2021,68(2):53-63. |
APA | Yang, Guirong,Pan, Zhaoxia,Zhang, Zhenghai,Song, Wenming,Ma, Ying,&Hao, Yuan.(2021).Mesoscopic transformation at initial corrosion stage of 20# steel in aqueous solution under gas-liquid two-phase stratified flow condition.ANTI-CORROSION METHODS AND MATERIALS,68(2),53-63. |
MLA | Yang, Guirong,et al."Mesoscopic transformation at initial corrosion stage of 20# steel in aqueous solution under gas-liquid two-phase stratified flow condition".ANTI-CORROSION METHODS AND MATERIALS 68.2(2021):53-63. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论